Abstract
Fe-based and Fe/Mo composite amorphous coatings were deposited on the surface of plain carbon steel substrates by atmospheric plasma spraying (APS). With increasing the Mo alloy content, the microstructure of the coatings revealed more dense structure. The porosities of composite coating were all less than those of Fe-based coating due to Mo alloy self-bonding performance. The ML-10 friction and wear tester was employed to investigate the wear behaviors of the coatings under dry sliding conditions. It was found that the mass loss of the resultant coatings decreased with increasing Mo-based powders into the feedstock. This was attributed to the reduction of the delaminations resulting from improved intersplat bond with Mo addition.
Similar content being viewed by others
References
P.W. Leech, X. S. Li, N. Alam, Wear 294–295 (2012) 380–386.
H. X. Li, P. He, T. S. Lin, F. Pan, J. C. Feng, Y. D. Huang, Trans. Nonferrous Met. Soc. China 22 (2012) 324–329.
O. Maranho, D. Rodrigues, M. Boccalini Jr., A. Sinatora, Wear 274–275 (2012) 162–167.
A. S. M. Ang, C. C. Berndt, P. Cheang, Surf. Coat. Technol. 205 (2011) 3260–3267.
G. Bolelli, T. Borner, F. Bozza, V. Cannillo, G. Grillo, L. Lusvarghi, Surf. Coat. Technol. 206 (2012) 4079–4094.
R. F. Li, Z. G. Li, J. Huang, Y. Y. Zhu, Appl. Surf. Sci. 258 (2012) 7956–7961.
M. Mulukutla, V. K. Kommineni, S. P. Harimkar, Appl. Surf. Sci. 258 (2012) 2886–2893.
A. Inoue, Acta Mater. 48 (2000) 279–306.
S. Yugeswaran, A. Kobayashi, K. Suresh, K. P. Rao, B. Subramanian, Appl. Surf. Sci. 258 (2012) 8460–8468.
Z. Zhou, L. Wang, D. Y. He, Y. B. Liu, G. Z. Zhang, Rare Metal Mater. Eng. 40 (2011) No. S3, 160–165.
A. H. Dent, A.J. Horlock, D. G. McCartney, S.J. Harris, Mater. Sci. Eng. A 283 (2000) 242–250.
Y. Wang, Y G. Zheng, W. Ke, W. H. Sun, W. L. Hou, X. C. Chang, J. Q. Wang, Corros. Sci. 53 (2011) 3177–3185.
A. Sova, D. Pervushin, I. Smurov, Surf. Coat. Technol. 205 (2010) 1108–1114.
F. Tarasi, M. Medraj, A. Dolatabadi, J. Oberste-Berghaus, C. Moreau, J. Eur. Ceram. Soc. 31 (2011) 2903–2913.
Z. Zhou, L. Wang, F. C. Wang, H. F. Zhang, Y. B. Liu, S. H. Xu, Surf. Coat. Technol. 204 (2009) 563–570.
A. Singh, S. R. Bakshi, A. Agarwal, S. P. Harimkar, Mater. Sci. Eng. A 527 (2010) 5000–5007.
X. Li, B. Yan, Q. W. Xiang, Y. X, Wang, J. Li, Rare Metal Mat. Eng. 40 (2011) 495–498.
CS. Kiminami, C. A. C. Souza, L. F. Bonavina, L. R. P. de Andrade Lima, S. Surinach, M. D. Baró, C. Bolfarini, W. J. Botta, J. Non-cryst. Solids 356 (2010) 2651–2657.
D. J. Branagan, W. D. Swank, D. C. Haggard, J. R. Fincke, Metall. Mater. Trans. A 32 (2001) 2616–2621.
A. Inoue, B. L. Shen, C. T. Chang, Acta Mater. 52 (2004) 4093–4099.
Z. Zhou, L. Wang, D. Y. He, F. C. Wang, Y. B. Liu, J. Therm. Spray Technol. 20 (2011) 344–350.
W. H. Lu, Y. P. Wu, J. J. Zhang, S. Hong, J. F. Zhang, G. Y. Li, J. Therm. Spray Technol. 20 (2011) 1063–1070.
C. P. Jiang, Y. Z. Xing, F. Y. Zhang, J. M. Hao, Int. J. Miner. Metall. Mater. 19 (2012) 657–662.
P. Niranatlumpong, H. Koiprasert, Surf. Coat. Technol. 205 (2010) 483–489.
Y. Z. Xing, Q. L. Wei, C. P. Jiang, J. M. Hao, Int. J. Miner. Metall. Mater. 19 (2012) 733–738.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Jiang, Cp., Xing, Yz., Zhang, Fy. et al. Wear Resistance and Bond Strength of Plasma Sprayed Fe/Mo Amorphous Coatings. J. Iron Steel Res. Int. 21, 969–974 (2014). https://doi.org/10.1016/S1006-706X(14)60170-9
Received:
Published:
Issue Date:
DOI: https://doi.org/10.1016/S1006-706X(14)60170-9