Investigation on Mechanical and Tribological Behaviors of PA6 and Graphite-Reinforced PA6 Polymer Composites

  • Research Article - Mechanical Engineering
  • Published:
Arabian Journal for Science and Engineering Aims and scope Submit manuscript

Abstract

In this paper, the effects of adding graphite on the mechanical and tribological properties of polyamide 6 (PA6)-based composites were investigated. PA6 was reinforced with graphite by varying the weight proportions. The test specimens for mechanical and tribological experiments were molded in an injection molding machine. The mechanical properties of PA6 and graphite-reinforced PA6 polymer composites were investigated in terms of tensile strength, impact and hardness tests. The PA6 composite containing 20 wt% graphite revealed the better mechanical behaviors. The wear test was observed by using a pin-on-disk machine under dry sliding conditions at 5, 10, 20 and 30 N applied load values and sliding speed of 1000, 1500 and 2000 rpm. Scanning electron microscopy was utilized to examine the worn surfaces microstructure and wear mechanisms before and after the tribological test. The results showed that the reinforced PA6 polymer composites with 20 wt% graphite enhanced the best tribological behavior. The addition of graphite enhances the life condition of normal PA6 to a greater extent. Also, this composite exhibits stronger interfacial bonding characteristics with improved wear resistance.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Similar content being viewed by others

References

  1. Unal H., Mimaroglu A.: Friction and wear performance of polyamide 6 and graphite and wax polyamide 6 composites under dry sliding conditions. Wear 289, 132–137 (2012)

    Article  Google Scholar 

  2. Hooke, C.J.; Mao, K.; Walton, D.: Measurement and prediction of the surface temperature in polymer gears and its relation to surface wear. J. Tribol. 115(1), 119–24 (1993)

  3. Wu X., Qiu J., Liu P., Sakai E.: Preparation and characterization of polyamide composites with modified graphite powders. J. Polym. Res. 20(11), 1–8 (2013)

    Article  Google Scholar 

  4. Shioyama H., Tatsumi K., Iwashita N., Fujita K., Sawada Y.: On the interaction between the potassium—GIC and unsaturated hydrocarbons. Synth. Metals 96(3), 229–233 (1998)

    Article  Google Scholar 

  5. Suresha B., Siddaramaiah S.K.S., Sampath Kumaran P.: Investigations on the influence of graphite filler on dry sliding wear and abrasive wear behaviour of carbon fabric reinforced epoxy composites. Wear 267, 1405–1414 (2009)

    Article  Google Scholar 

  6. Kalaitzidou K., Fukushima H., Drzal L.T.: A new compounding method for exfoliated graphite-polypropylene nanocomposites with enhanced flexural properties and lower percolation threshold. Compos. Sci. Technol. 67, 2045–2051 (2007)

    Article  Google Scholar 

  7. Velde, F.Van De ; Baets, P. De : The friction and wear behaviour of polyamide 6 sliding against steel at low velocity under very high contact pressures. Wear 209(1), 106–114 (1997)

  8. Palabiyik M., Bahadur S.: Mechanical and tribological properties of polyamide 6 and high density polyethylene polyblends with and without compatibilizer. Wear 246(1), 149–158 (2000)

    Article  Google Scholar 

  9. Xu Z., Gao C.: In situ polymerization approach to graphene-reinforced nylon-6 composites. Macromolecules 43(16), 6716–6723 (2010)

    Article  Google Scholar 

  10. Watanabe M., Yamaguchi H.: The friction and wear properties of nylon. Wear 110(3), 379–388 (1986)

    Article  Google Scholar 

  11. Tanaka K.: Transfer of semicrystalline polymers sliding against a smooth steel surface. Wear 75(1), 183–199 (1982)

    Article  Google Scholar 

  12. Bahadur, S.; Tabor, D.: Role of fillers in the friction and wear behavior of high-density polyethylene. In: Lee, L.-H. (ed.) Polymer Wear and Its Control. ACS Symposium Series, vol. 287, pp. 253–268 (1985)

  13. Stokes V.K., Inzinna L.P., Liang E.W., Trantina G.G., Woods J. T.: A phenomenological study of the mechanical properties of long-fiber filled injection-molded thermoplastic composites. Polym. Compos. 21(5), 696–710 (2000)

    Article  Google Scholar 

  14. Shin M.W., Kim S.S., Jang H.: Friction and wear of polyamide 66 with different weight average molar mass. Trib. Lett. 44(2), 151–158 (2011)

    Article  Google Scholar 

  15. Palabiyik M., Bahadur S.: Mechanical and tribological properties of polyamide 6 and high density polyethylene polyblends with and without compatibilizer. Wear 246(1), 149–158 (2000)

    Article  Google Scholar 

  16. Palabiyik M., Bahadur S.: Tribological studies of polyamide 6 and high-density polyethylene blends filled with PTFE and copper oxide and reinforced with short glass fibers. Wear 253(3), 369–376 (2002)

    Article  Google Scholar 

  17. Jia B.B., Li T.S., Liu X.J., Cong P.H.: Tribological behaviors of several polymer–polymer sliding combinations under dry friction and oil-lubricated conditions. Wear 262(11), 1353–1359 (2007)

    Article  Google Scholar 

  18. Cong P., Xiang F., Liu X., Li T.: Effect of crystalline form on the tribological properties of PA46/HDPE polyblends. Wear 265(7), 1106–1113 (2008)

    Article  Google Scholar 

  19. Li D.X., Deng X., Wang J., Yang J., Li X.: Mechanical and tribological properties of polyamide 6-polyurethane block copolymer reinforced with short glass fibers. Wear 269(3), 262–268 (2010)

    Article  Google Scholar 

  20. Li J., Sheng X.H.: The effect of PA6 content on the mechanical and tribological properties of PA6 reinforced PTFE composites. J. Mater. Eng. Perform. 19(3), 342–346 (2010)

    Article  MathSciNet  Google Scholar 

  21. Liu S.P., Hwang S.S., Yeh J.M., Hung C.C.: Mechanical properties of polyamide-6/montmorillonite nanocomposites—prepared by the twin-screw extruder mixed technique. Int. Commun. Heat Mass Transf. 38(1), 37–43 (2011)

    Article  Google Scholar 

  22. Pan B., Zhang S., Li W., Zhao J., Liu J., Zhang Y.: Tribological and mechanical investigation of MC nylon reinforced by modified graphene oxide. Wear 294, 395–401 (2012)

    Article  Google Scholar 

  23. Konieczny J., Chmielnicki B., Tomiczek A.: Evaluation of selected properties of PA6-copper/graphite composite. J. Achiev. Mater. Manuf. Eng. 60(1), 23–30 (2013)

    Google Scholar 

  24. Li D.X., You Y.L., Deng X., Li W.J., Xie Y.: Tribological properties of solid lubricants filled glass fiber reinforced polyamide 6 composites. Mater. Des. 46, 809–815 (2013)

    Article  Google Scholar 

  25. Li M., Wan Y., Gao Z., Xiong G., Wang X., Wan C., Luo H.: Preparation and properties of polyamide 6 thermal conductive composites reinforced with fibers. Mater. Des. 51, 257–261 (2013)

    Article  Google Scholar 

  26. Demir Z.: Tribological performance of polymer composites used in electrical engineering applications. Bull. Mater. Sci. 36(2), 341–344 (2013)

    Article  Google Scholar 

  27. Jia Z., Hao C., Yan Y., Yang Y.: Effects of nanoscale expanded graphite on the wear and frictional behaviors of polyimide-based composites. Wear 338, 282–287 (2015)

    Article  Google Scholar 

  28. Özerol E.A., Şenkal B.F., Okutan M.: Preparation and characterization of graphite composites of polyaniline. Microelectron. Eng. 146, 76–80 (2015)

    Article  Google Scholar 

  29. Gong L., Yin B., Li L.P., Yang M.B.: Nylon-6/graphene composites modified through polymeric modification of graphene. Compos. Part B Eng. 73, 49–56 (2015)

    Article  Google Scholar 

  30. Faghihi M., Shojaei A., Bagheri R.: Characterization of polyamide 6/carbon nanotube composites prepared by melt mixing-effect of matrix molecular weight and structure. Compos. Part B: Eng. 78, 50–64 (2015)

    Article  Google Scholar 

  31. Fasahat F., Dastjerdi R., Mojtahedi M.R.M., Hoseini P.: Wear properties of high speed spun multi-component PA6 nanocomposite fabrics; abrasion resistance mechanism of nanocomposites. Wear 322, 17–125 (2015)

    Google Scholar 

  32. Zhang, X.R.; Pei, X.Q.;Wang, Q.H.;Wang, T.M.; Chen, S.B.: The friction and wear properties of carbon nanotubes/graphite/carbon fabric reinforced phenolic polymer composites. Adv. Compos. Mater. 24 (Suppl 1), 147–159 (2015)

  33. Boparai K., Singh R., Singh H.: Comparison of tribological behaviour for Nylon6-Al-Al2O3 and ABS parts fabricated by fused deposition modelling: This paper reports a low cost composite material that is more wear-resistant than conventional ABS. Virtual Phys. Prototyp. 10(2), 59–66 (2015)

    Article  Google Scholar 

Download references

Author information

Authors and Affiliations

  1. Department of Mechanical Engineering, Latha Mathavan Engineering College, Madurai, Tamil Nadu, 625301, India

    S. Sathees Kumar

  2. Department of Mechanical Engineering, Thiagarajar College of Engineering, Madurai, Tamil Nadu, 625015, India

    G. Kanagaraj

Authors
  1. S. Sathees Kumar
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. G. Kanagaraj
    View author publications

    You can also search for this author in PubMed Google Scholar

Corresponding author

Correspondence to S. Sathees Kumar.

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Sathees Kumar, S., Kanagaraj, G. Investigation on Mechanical and Tribological Behaviors of PA6 and Graphite-Reinforced PA6 Polymer Composites. Arab J Sci Eng 41, 4347–4357 (2016). https://doi.org/10.1007/s13369-016-2126-2

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s13369-016-2126-2

Keywords

Search

Navigation