Protected silver coatings for reflectors

  • Original Paper
  • Published:
CEAS Space Journal Aims and scope Submit manuscript

Abstract

For ground- and spaced-based applications, Ag-coated reflectors are indispensable because of their high reflectivity. The transport, assembly, and storage of these reflectors take places over a long period before they are finally commissioned for application. To endure this period without a decrease of reflectivity, protective coatings with a final layer, which offers a high resistance to aqueous solutions, and a low mechanical stress should be used. These criteria were taken into account for the selection of a final layer for a protected Ag coating, which was applied for reflectors utilized in the CRIRES+-instrument (an IR spectrograph used at the VLT). Reactively sputtered Al2O3, SiO2 and Si3N4 layers were investigated with regard to these criteria. In aqueous (alkaline) solutions, the investigated Si3N4 layers are more stable than the SiO2 layers and the SiO2 layers more stable than the Al2O3 layers. This shows the influence of the intrinsic material properties. The mechanical stress of the sputtered layers depends on the deposition conditions and thus on the selected parameters. A Si3N4 layer with a high resistance to aqueous (alkaline) solutions also offers low and stable mechanical stress. Therefore, the deposition parameters used for this layer were applied for sputtering the final layer of the protected Ag coating for the reflectors.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Fig. 1
Fig. 2
Fig. 3
Fig. 4
Fig. 5

Similar content being viewed by others

References

  1. Wilson, R.N.: Reflecting Telescope Optics II. Springer, Berlin Heidelberg (2001)

    Google Scholar 

  2. Jean, M.B., Ashley, E.J.: Infrared reflectance and emittance of silver and gold evaporated in ultrahigh vacuum. Appl. Opt. 4(2), 221–224 (1965)

    Article  Google Scholar 

  3. Thomas, N., Wolfe, J.: UV-shifted durable silver coating for astronomical mirrors. Proc. SPIE 4003, 312–323 (2000)

    Article  Google Scholar 

  4. Veleva, L., Valdez, B., Lopez, G., et al.: Atmospheric corrosion of electro-electronics metals in urban desert simulated indoor environment. Corros. Eng. Sci. Technol. 43(2), 149–155 (2013)

    Article  Google Scholar 

  5. Vargas, O.L., Valdez, S.B., Veleva, M.L., et al.: The corrosion of silver in indoor conditions of an assembly process in the microelectronics industry. Anti-Corrosion Meth. Mater. 56(4), 218–225 (2009)

    Article  Google Scholar 

  6. Jobst, P.J., Stenzel, O., Schürmann, M., et al.: Optical properties of unprotected and protected sputtered silver films: surface morphology vs. UV/VIS reflectance. Adv. Opt. Technol. 3(1), 91–102 (2014)

    Google Scholar 

  7. Thomas, N.L., Siekhaus, W.J., Farmer, J.C., et al.: Prevention of corrosion of silver reflectors for the National Ignition Facility. Proc. SPIE 3427, 394–400 (1998)

    Article  Google Scholar 

  8. Hass, G., Heaney, J.B., Herzig, H., et al.: Reflectance and durability of Ag mirrors coated with thin layers of Al2O3 plus reactively deposited silicon oxide. Appl. Opt. 14(11), 2639–2644 (1975)

    Article  Google Scholar 

  9. Pellicori, S.F.: Scattering defects in silver mirror coatings. Appl. Opt. 19(18), 3096–3098 (1980)

    Article  Google Scholar 

  10. Vucina, T., Boccas, M., Araya, C., et al.: Gemini primary mirror in situ wash. Proc. SPIE 7012, 1–13 (2008)

    Google Scholar 

  11. Chu, C.-T., Fuqua, P.D., Barrie, J.D.: Corrosion characterization of durable silver coatings by electrochemical impedance spectroscopy and accelerated environmental testing. Appl. Opt. 45(7), 1583–1593 (2006)

    Article  Google Scholar 

  12. Folgner, K.A., Chu, C.-T., Lingley, Z.R., et al.: Environmental durability of protected silver mirrors prepared by plasma beam sputtering. Appl. Opt. 56(4), 75–86 (2017)

    Article  Google Scholar 

  13. Barrie, J.D., Fuqua, P.D., Folgner, K.A., et al.: Control of stress in protected silver mirrors prepared by plasma beam sputtering. Appl. Opt. 50(9), 135–140 (2011)

    Article  Google Scholar 

  14. Schwinde, S., Schürmann, M., Jobst, P.J., et al.: Description of particle induced damage on protected silver coatings. Appl. Opt. 54, 4966–4971 (2015)

    Article  Google Scholar 

  15. Herrmanna, M., Schilma, J., Michaela, G., et al.: Corrosion of silicon nitride materials in acidic and basic solutions and under hydrothermal conditions. J. Eur. Ceram. Soc. 23, 585–594 (2003)

    Article  Google Scholar 

  16. Lin, C.-H., Komeya, K., Meguro, T., et al.: Corrosion resistance of wear resistant silicon nitride ceramics in various aqueous solutions. J. Ceram. Soc. Japan 111, 452–456 (2003)

    Article  Google Scholar 

  17. Vogel, W.: Glaschemie. Springer-Verlag, Berlin (1992)

    Book  Google Scholar 

  18. Salh, R.: Defect related luminescence in silicon dioxide network: a review. InTech-Verlag, Rijeka (2011)

    Book  Google Scholar 

  19. Waters, P., Volinsky, A.A.: Stress and moisture effects on thin film buckling delamination. Exp. Mech. 47, 163–170 (2007)

    Article  Google Scholar 

  20. Leplan, H., Geenen, B., Robic, J.Y., et al.: Residual stresses in evaporated silicon dioxide thin films: correlation with deposition parameters and aging behavior. J. Appl. Phys. 78(2), 962–968 (1995)

    Article  Google Scholar 

  21. Schwinde, S., Schürmann, M., Kaiser, N., et al.: Investigation of SiO2–Al2O3 nanolaminates for protection of silver reflectors. Appl. Opt. 56, 41–46 (2017)

    Article  Google Scholar 

  22. Berg, S., Nyberg, T.: Fundamental understanding and modeling of reactive sputtering processes. Thin Solid Films 476, 215–230 (2005)

    Article  Google Scholar 

  23. Sheikh, D.A., Connell, S.J., Dummer, R.S.: Durable silver coating for Kepler Space Telescope primary mirror. Proc. SPIE 7010, 1–5 (2008)

    Google Scholar 

  24. Kinast, J., Schlegel, R., Kleinbauer, K., Steinkopf, R., Follert, R., et al.: Manufacturing of aluminum mirrors for cryogenic applications. Proc. SPIE 10706, 107063G-1–107063G-7 (2018)

    Google Scholar 

  25. Dorn, R.J., Anglada-Escude, G., Baade, D., et al.: CRIRES+: exploring the cold universe at high spectral resolution. Messenger 156, 7–11 (2014)

    Google Scholar 

  26. Berg, S., Larsson, T., Nender, C., et al.: Predicting thin-film stoichiometry in reactive sputtering. J. Appl. Phys. 63, 887–891 (1988)

    Article  Google Scholar 

  27. Särhammar, E., Strijckmans, K., Nyberg, T., et al.: A study of the process pressure influence in reactive sputtering aiming at hysteresis elimination. Surf. Coat. Technol. 232, 357–361 (2013)

    Article  Google Scholar 

  28. Software: OptiChar by A.V. Tikhonravov and M.K.Trusbetskov; Module of the software package Optilayer; OptiLayer GmbH; Version 12.12 (2013)

  29. User manual: Tencor FLX-2320 user manual. Thin Film Stress Measurement. Tencore Instruments, 9.1–9.3 (1995)

  30. Depla, D.: Magnetrons, reactive gases and sputtering. Ghent University Belgium, Ghent (2014)

    Google Scholar 

  31. Huheey, J.E., Keiter, E.A., Keiter, R.L.: Anorganische Chemie: Prinzipien von Struktur und Reaktivität. de Gruyter, Berlin (2003)

    Google Scholar 

  32. Cartledge, G.H.: “Studies on the Periodic system—the ionic potential as a periodic function”, 1. J. Am. Chem. Soc. 50(11), 2855–2863 (1928)

    Google Scholar 

  33. Sree, K.S.: Principle of physical vapor deposition of thin films. Elsevier, New York (2006)

    Google Scholar 

  34. Blasek, G., Bräuer, G.: Vakuum Plasma Technologien: Beschichtung und Modifizierung von Oberflächen. Eugen G. Leutze Verlag 87–101 (2010)

  35. Thornton, J.A.: Influence of substrate temperature and deposition rate on structure of thick sputtered Cu coatings. J. Vacuum Sci. Technol. 11, 666–670 (1974)

    Article  Google Scholar 

  36. Hirsch, E.H.: Stress in porous thin films through absorption of polar molecules. J. Phys. D Appl. Phys. 13, 2081–2094 (1980)

    Article  Google Scholar 

  37. Stolz, C.J., Taylor, J.R., Eickelberg, W.K., et al.: Effects of vacuum exposure on stress and spectral shift of high reflective coatings. Appl. Opt. 32(28), 5666–5672 (1993)

    Article  Google Scholar 

  38. Nishikawa, T., Ono, H., Murotani, H., et al.: Analysis of long-term internal stress and film structure of SiO2 optical thin films. Appl. Opt. 50(9), 210–216 (2011)

    Article  Google Scholar 

  39. Scherer, K., Nouvelot, L., Lacan, P., et al.: Optical and mechanical characterization of evaporated SiO2 layers. Long-term evolution. Appl. Opt. 35(25), 5067–5072 (1996)

    Article  Google Scholar 

  40. Schulz, U., Jakobs, S., Norbert, K.: SiO2 protective coatings on plastic optics deposited with plasma-lAD. Proc. SPIE 2776, 169–174 (1996)

    Article  Google Scholar 

  41. Bräuer, G., Szczyrbowski, J., Teschner, G.: Mid frequency sputtering—a novel tool for large area coating. Surf. Coat. Technol. 94–95, 658–662 (1997)

    Article  Google Scholar 

  42. Besland, M.-P., Lapeyrade, M., Delmotte, F., et al.: Interpretation of stress variation in silicon nitride films deposited by electron cyclotron resonance plasma. J. Vacuum Sci. Technol. A 22(5), 1962–1970 (2004)

    Article  Google Scholar 

  43. Schürmann, M., Schwinde, S., Kaiser, N.: Optical element comprising a reflective coating Patent specification: EP3158370A1 (2015)

  44. Schwinde, S., Schürmann, M., Kaiser, N., et al.: Protected and enhanced silver for mirrors: damage mechanisms and how to prevent them. Proc. SPIE 9627, 96271R-1–96271R-6 (2015)

    Google Scholar 

Download references

Author information

Authors and Affiliations

  1. Fraunhofer Institute for Applied Optics and Precision Engineering IOF, Albert-Einstein-Strasse 7, 07745, Jena, Germany

    Stefan Schwinde, Mark Schürmann, Ralph Schlegel, Jan Kinast & Norbert Kaiser

  2. European Southern Observatory ESO, Karl-Schwarzschild-Straße 2, 85748, Garching bei Muenchen, Germany

    Reinhold J. Dorn, Jean Louis Lizon & Sebastien Tordo

Authors
  1. Stefan Schwinde
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. Mark Schürmann
    View author publications

    You can also search for this author in PubMed Google Scholar

  3. Ralph Schlegel
    View author publications

    You can also search for this author in PubMed Google Scholar

  4. Jan Kinast
    View author publications

    You can also search for this author in PubMed Google Scholar

  5. Reinhold J. Dorn
    View author publications

    You can also search for this author in PubMed Google Scholar

  6. Jean Louis Lizon
    View author publications

    You can also search for this author in PubMed Google Scholar

  7. Sebastien Tordo
    View author publications

    You can also search for this author in PubMed Google Scholar

  8. Norbert Kaiser
    View author publications

    You can also search for this author in PubMed Google Scholar

Corresponding author

Correspondence to Stefan Schwinde.

Additional information

Publisher's Note

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Schwinde, S., Schürmann, M., Schlegel, R. et al. Protected silver coatings for reflectors. CEAS Space J 11, 579–587 (2019). https://doi.org/10.1007/s12567-019-00257-9

Download citation

  • Received:

  • Revised:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s12567-019-00257-9

Keywords

Search

Navigation