Abstract
Jute fabric (hessian cloth) was grafted with 2-hydroxy ethylacrylate (HEA) and aliphatic urethane diacrylate oligomer (M-1200) under UV radiation at different intensities (16, 20, 30, 40, 50, and 60 pass) in order to improve the mechanical and electrical properties. The concentrations of the monomer (HEA), and oligomer (M1200), radiation dose, and soaking time were optimized with respect to mechanical property such as tensile strength (TS) of the treated and untreated hessian cloth. The 73 % HEA, 25 % oligomer (M-1200) and 2 % photoinitiator (Darocur-1116) in 1 minute soaking time showed the highest TS at 50th UV pass. The electrical properties such as dielectric constant and loss tangent of both treated and untreated sample were measured at frequency 10 kHz with the variation of temperature. It was observed that dielectric constant and loss tangent increased with increasing temperature up to the transition temperature and then decreased.
Similar content being viewed by others
References
M. M. Hassan, M. R. Islam, M. A. Sawpan, and M. A. Khan, J. Appl. Polym. Sci., 89, 3530 (2003).
M. A. Khan, L. R. Das, A. H. Khan, F. Ahmed, and S. M. B. Rahman, J. Appl. Polym. Sci., 89, 655 (2003).
K. M. A. Idriss, M. K. Uddin, M. I. U. Bhuiyan, and M. A. Khan, J. Appl. Polym. Sci., 54, 303 (1994).
M. A. Khan, S. Shehrzade, M. Sarwar, U. Chowdhury, and M. M. Rahman, J. Polym. Environ., 9, 115 (2002).
M. A. Khan, S. Shehrzade, and M. M. Hassan, J. Appl. Polym. Sci., 92, 18 (2004).
M. A. Khan, M. M. Hossain, M. A. Hossain, and K. M. I. Ali, Polym.-Plast. Technol. Eng., 36, 285 (1997).
M. A. Khan, K. M. I. Ali, M. R. Al-Immam, and R. Mannan, J. Polym.-Plast. Technol. Eng., 36, 89 (1997).
M. A. Khan, M. N. Islam, and K. M. I. Ali, Radiat. Phys. Chem., 48, 337 (1996).
M. M. Hassan, M. R. Islam, and M. A. Khan, J. Adhesion Sci. Technol., 17, 737 (2003).
M. A. Khan, G. Hinrichsen, and L. T. Drzal, J. Mater. Sci. Lett., 20, 1711 (2001).
M. A. Khan, M. K. Uddin, M. N. Islam, and K. M. I. Ali, J. Appl. Polym. Sci., 58, 31 (1995).
M. A. Khan, M. K. Uddin, M. N. Islam, and K. M. I. Ali, J. Appl. Polym. Sci., 58, 31 (2003).
M. A. Khan, M. Hossain, and K. M. I. Ali, J. Appl. Polym. Sci., 74, 900 (1999).
M. A. Khan and M. M. Hasan, Polymer Surface Modification: Relevance to Adhesion, VSP, 3, 263 (2004).
S. Mishra, A. K. Mohanty, M. Drzal, S. Parija, S. K. Nayak, and S. S. Tripathy, Compos. Sci. Technol., 63, 1377 (2003).
M. A. Khan, M. M. Hassan, and L. T. Drazal, Composites: Part A, 36, 71 (2005).
T. A. Bullions, R. A. Gillespie, J. Price-O’Brien, and A. C. Loos, J. Appl. Polym. Sci., 92, 3771 (2004).
M. A. Khan, R. A. Khan, H. U. Zaman, M. A. Hossain, and A. H. Khan, Journal of Reinforced Plastics and Composites, 28, 1651 (2009).
K. M. I. Ali, M. A. Khan, and M. N. Islam, Polym. Plast. Technol. Eng., 35, 299 (1996).
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Khan, M.A., Majumder, S.C., Arifur Rahman, M. et al. Mechanical and electrical properties of photocured jute fabric with 2-hydroxy ethylacrylate. Fibers Polym 11, 391–397 (2010). https://doi.org/10.1007/s12221-010-0391-3
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s12221-010-0391-3