Abstract
In this study, various coatings including Mo, Ti, Y2O3-stabilized ZrO2 (YSZ)/Ti films were deposited on the CoSb3 substrate using magnetron sputtering to suppress the sublimation of antimony in CoSb3 during thermal aging tests. The microstructure and growth of films were observed using scanning electron and atomic force microscopes. The thermal aging behavior of CoSb3 coated with various films was investigated through an accelerated experiment at 923 K for 24 h. The weight loss of CoSb3 decreased with the thickness of coatings increasing. Among these films, the YSZ/Ti film can suppress the sublimation of antimony in CoSb3 more effectively. Compared with the uncoated CoSb3 material, the degradation of thermoelectric properties for coated CoSb3 samples decreased slowly after the accelerated thermal aging test.
Similar content being viewed by others
References
Q.H. Zhang, X. Ai, L.J. Wang, Y.X. Chang, W. Luo, W. Jiang, and L.D. Chen, Adv. Funct. Mater. 25, 966 (2015).
W.S. Liu, X. Yan, G. Chen, and Z.F. Ren, Nano. Energy 1, 42 (2012).
H. Alam and S. Ramakrishna, Nano. Energy 2, 190 (2013).
Q.H. Zhang, X. Ai, W.J. Wang, L.J. Wang, and W. Jiang, Acta Mater. 73, 37 (2014).
S.K. Bux, J.-P. Fleurial, and R.B. Kaner, Chem. Commun. 46, 8311 (2010).
B.C. Sales, D. Mandrus, and R.K. Williams, Science 272, 1325 (1996).
S.Q. Bai, Y.Z. Pei, L.D. Chen, W.Q. Zhang, X.Y. Zhao, and J. Yang, Acta Mater. 57, 3135 (2009).
X. Shi, J. Yang, J.R. Salvador, and R. James, J. Am. Chem. Soc. 133, 7837 (2011).
Y.T. Qiu, L.L. Xi, X. Shi, and L. Chen, Adv. Funct. Mater. 23, 3194 (2013).
H.H. Saber, M.S. El-Genk, and T. Caillat, Energy Convers. Manag. 48, 555 (2007).
E. Godlewska, K. Zawadzka, K. Mars, R. Mania, and K. Wojciechowski, Oxid. Met. 74, 205 (2010).
H. Dong, X. Li, Y. Tang, J. Zou, and L. Chen, J. Alloys Compd. 527, 247 (2012).
H. Dong, X. Li, X. Huang, Y. Zhou, W. Jiang, and L. Chen, Ceram. Int. 39, 4551 (2013).
D.G. Zhao, M. Zuo, J.F. Leng, and H.R. Geng, Intermetallics 40, 71 (2013).
D.G. Zhao, M. Zuo, Z.Q. Wang, X.Y. Teng, and H.R. Geng, Appl. Surf. Sci. 305, 86 (2014).
J.A. Thornton, Annu. Rev. Mater. Res. 7, 239 (2010).
D.H. Kuo and C.H. Chien, Thin Solid Films 40, 429 (2003).
Y.L. Jeyachandran, B. Karunagaran, S.K. Narayandass, and D. Mangalaraj, Mater. Sci. Eng. A 458, 361 (2007).
D. Zhao, C. Tian, S. Tang, Y. Liu, and L. Chen, J. Alloys Compd. 509, 3166 (2010).
G.I. Cubillos, M. Bethencourt, J.J. Olaya, J.E. Alfonso, and J.F. Marco, Appl. Surf. Sci. 309, 181 (2014).
Acknowledgements
Financial support was received from the Opening Project of the State Key Laboratory of High Performance Ceramics and Superfine Microstructure (SKL201405SIC) and National Natural Science Foundation of China (51202088). The authors would like to thank the help from Shandong University and Shandong Research and Design Institute of Industrial Ceramics for the measurement of TE properties.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Zhao, D., Wu, D., Ning, J. et al. Protective Properties of Various Coatings on CoSb3 Thermoelectric Material. J. Electron. Mater. 46, 3036–3042 (2017). https://doi.org/10.1007/s11664-016-5141-x
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11664-016-5141-x