Anodized Macroporous Silicon Anode for Integration of Lithium-Ion Batteries on Chips

  • Published:
Journal of Electronic Materials Aims and scope Submit manuscript

Macroporous silicon membranes were investigated as anodes for potential integration of lithium-ion batteries on chips. Free-standing and partially etched porous silicon membranes were fabricated from a p-type silicon wafer by using electrochemical anodization. Free-standing porous membranes were achieved with high aspect ratio of 40, average pore size of 1 μm, porosity around ~70%, and wall thickness of less than 0.1 μm. Lithium storage capacity was quantified by galvanostatic discharge/charge measurements, showing specific capacity of 1425 mAh/g with Coulombic efficiency of 81% in the first discharge/charge cycle. The discharge/charge capacity was reduced as the charge rate increased, and the capacity fading was much less pronounced at high charge rate. Morphological analyses showed an increase of surface roughness and reduction of porosity after lithiation/delithiation cycling.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Similar content being viewed by others

References

  1. T. Ripenbein, D. Golodnitsky, M. Nathan, and E. Peled, Electrochim. Acta 56, 37 (2010).

    Article  CAS  Google Scholar 

  2. T.-M. Tarascon and A. Armand, Nature 414, 359 (2001).

    Article  CAS  Google Scholar 

  3. A.S. Arico, P. Bruce, J.M. Tarascon, and W. Van Schalkwijk, Nat. Mater. 4, 366 (2005).

    Article  CAS  Google Scholar 

  4. X.H. Liu, L.Q. Zhang, L. Zhong, Y. Liu, H. Zheng, J.W. Wang, J.H. Cho, S.A. Dayeh, S.T. Picraux, J.P. Sullivan, S.X. Mao, Z.Z. Ye, and J.Y. Huang, Nano Lett. 11, 2251 (2011).

    Article  CAS  Google Scholar 

  5. X.H. Liu, H. Zheng, L. Zhong, S. Huang, K. Karki, L.Q. Zhang, Y. Liu, A. Kushima, W.T. Liang, J.W. Wang, J.-H. Cho, E. Epstein, S.A. Dayeh, S.T. Picraux, T. Zhu, J. Li, J.P. Sullivan, J. Cumings, C. Wang, S.X. Mao, Z.Z. Ye, S. Zhang, and J.Y. Huang, Nano Lett. 11, 3312 (2011).

    Article  CAS  Google Scholar 

  6. U. Kasavajjula, C. Wang, and A.J. Appleby, J. Power Sour. 163, 1003 (2007).

    Article  CAS  Google Scholar 

  7. H. Li, X. Huang, L. Chen, G. Zhou, Z. Zhang, D. Yu, Y.J. Mo, and N. Pei, Solid State Ionics 135, 181 (2000).

    Article  CAS  Google Scholar 

  8. M. Green, E. Fielder, B. Scrosati, M. Wachtler, and J.S. Morenob, Electrochem. Solid-State Lett. 6, A75 (2003).

    Article  CAS  Google Scholar 

  9. M. Yoshio, T. Tsumura, and N. Dimov, J. Power Sour. 146, 10 (2005).

    Article  CAS  Google Scholar 

  10. J. Li, A. Dozier, Y. Li, F. Yang, and Y. Cheng, J. Electrochem. Soc. 158, A689 (2011).

    Article  CAS  Google Scholar 

  11. S.K. Lee, M.T. McDowell, L.A. Berla, W.D. Nix, and Y. Cui, Proc. Natl. Acad. Sci. 109, 4080 (2012).

    CAS  Google Scholar 

  12. J. Graetz, C.C. Ahn, R. Yazami, and B. Fultz, Electrochem. Solid-State Lett. 6, A194 (2003).

    Article  CAS  Google Scholar 

  13. L.B. Chen, J.Y. Xie, H.C. Yu, and T.H. Wang, J. Appl. Electrochem. 39, 1157 (2009).

    Article  CAS  Google Scholar 

  14. N. Ding, J. Xua, Y. Yao, G. Wegner, I. Lieberwirth, and C. Chen, J. Power Sour. 192, 644 (2009).

    Article  CAS  Google Scholar 

  15. H. Jia, P. Gao, J. Yang, J. Wang, Y. Nuli, and Z. Yang, Adv. Energy Mater. 1, 1036 (2011).

    Article  CAS  Google Scholar 

  16. L.F. Cui, R. Ruffo, C.K. Chan, H. Peng, and Y. Cui, Nano Lett. 9, 491 (2009).

    Article  CAS  Google Scholar 

  17. C.K. Chan, H.L. Peng, G. Liu, K. McIlwrath, X.F. Zhang, R.A. Huggins, and Y. Cui, Nat. Nanotechnol. 3, 31 (2008).

    Article  CAS  Google Scholar 

  18. K. Peng, J. Jie, W. Zhang, and S.T. Lee, Appl. Phys. Lett. 93, 033105 (2008).

    Article  Google Scholar 

  19. M. Leisner, A. Cojocaru, E. Ossei-Wusu, J. Carstensen, and H. Foll, Nanoscal. Res. Lett. 5, 1502 (2010).

    Article  CAS  Google Scholar 

  20. E. Ossei-Wusu, A. Cojocaru, H. Hartz, J. Carstensen, and H. Föll, Phys. Stat. Solidi (a) 208, 1417 (2011).

    Article  CAS  Google Scholar 

  21. H. Föll, H. Hartz, E. Ossei-Wusu, J. Carstensen, and O. Riemenschneider, Phys. Stat. Solidi RRL 4, 4 (2010).

    Article  Google Scholar 

  22. H. Föll, J. Carstensen, E. Ossei-Wusu, A. Cojocaru, E. Quiroga-Gonzalez, and G. Neumann, J. Electrochem. Soc. 158, A580 (2011).

    Article  Google Scholar 

  23. M.-H. Park, M.G. Kim, J. Joo, K. Kim, J. Kim, S. Ahn, and Y. Cui, Nano Lett. 9, 3844 (2009).

    Article  CAS  Google Scholar 

  24. H.C. Shin, J.A. Corno, J.L. Gole, and M.L. Liu, J. Power Sour. 139, 314 (2005).

    Article  CAS  Google Scholar 

  25. D.K. Kang, J.A. Corno, J.L. Gole, and H.C. Shin, J. Electrochem. Soc. 155, A276 (2008).

    Article  CAS  Google Scholar 

  26. M. Thakur, M. Isaacson, S. Sinsabaugh, M.S. Wong, and S.L. Biswal, J. Power Sour. 205, 426 (2012).

    Article  CAS  Google Scholar 

  27. E.V. Astrova, G.V. Fedulova, I.A. Smirnova, A.D. Remenyuk, T.L. Kulova, and A.M. Skundin, Tech. Phys. Lett. 37, 731 (2011).

    Article  CAS  Google Scholar 

  28. http://www.ctcms.nist.gov/oof/oof2/.

  29. E.A. Ponomarev and C. Levy-Clement, J. Porous Mater. 7, 51 (2000).

    Article  CAS  Google Scholar 

  30. M.N. Obrovac and L.J. Krause, J. Electrochem. Soc. 154, A103 (2007).

    Article  CAS  Google Scholar 

  31. H. Wu, G. Chan, J.W. Choi, I. Ryu, Y. Yao, M.T. McDowell, S.W. Lee, A. Jackson, Y. Yang, L. Hu, and Y. Cui, Nat. Nanotechnol. 25, 1 (2012).

    Google Scholar 

  32. X.H. Liu, L. Zhong, S. Huang, S.X. Mao, T. Zhu, and J.Y. Huang, ACS Nano 6, 1522 (2012).

    Article  CAS  Google Scholar 

  33. J. Xie, N. Imanishi, T. Zhang, A. Hirano, Y. Takeda, and O. Yamamoto, Mater. Chem. Phys. 120, 421 (2010).

    Article  CAS  Google Scholar 

  34. R. Ruffo, S.S. Hong, C.K. Chan, R.A. Huggins, and Y. Cui, J. Phys. Chem. C 113, 11390 (2009).

    Article  CAS  Google Scholar 

  35. S.K. Soni, B.W. Sheldon, X.C. Xiao, and A. Tokranov, Scripta Mater. 64, 307 (2011).

    Article  CAS  Google Scholar 

Download references

Author information

Authors and Affiliations

  1. Department of Electrical Engineering, Wright State University, Dayton, OH, USA

    Xida Sun & Yan Zhuang

  2. Department of Mechanical and Materials Engineering, Wright State University, Dayton, OH, USA

    Hong Huang

  3. Department of Electrical Engineering, Grove City College, Grove City, PA, USA

    Kuan-Lun Chu

Authors
  1. Xida Sun
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. Hong Huang
    View author publications

    You can also search for this author in PubMed Google Scholar

  3. Kuan-Lun Chu
    View author publications

    You can also search for this author in PubMed Google Scholar

  4. Yan Zhuang
    View author publications

    You can also search for this author in PubMed Google Scholar

Corresponding author

Correspondence to Yan Zhuang.

Rights and permissions

Reprints and permissions

About this article

Cite this article

Sun, X., Huang, H., Chu, KL. et al. Anodized Macroporous Silicon Anode for Integration of Lithium-Ion Batteries on Chips. J. Electron. Mater. 41, 2369–2375 (2012). https://doi.org/10.1007/s11664-012-2147-x

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s11664-012-2147-x

Keywords

Search

Navigation