Correlations Between the Microstructure and Fatigue Life of Near-Eutectic Sn-Ag-Cu Pb-Free Solders

  • Published:
Journal of Electronic Materials Aims and scope Submit manuscript

Abstract

Relationships between the microstructure of near-eutectic Sn-Ag-Cu Pb-free solder joints and room-temperature fatigue lifetimes were studied. Correlations between the lifetimes of single Sn grained, SAC205 solder joints with the orientation of the Sn grain, and with differences in Ag3Sn and Cu6Sn5 precipitate microstructures were sought. Correlations between the number of Sn grains and fatigue life were observed. Surprisingly, it was found that Ag3Sn precipitates were highly segregated from Cu6Sn5 precipitates on a length scale of approximately 20 μm. Furthermore, large (factor of two) variations of the Sn dendrite arm size were observed within given samples. Such variations in values of dendrite arm size within a single sample were much larger than observed variations of this parameter between individual samples. Few significant differences were observed in the average size of precipitates in different samples. Although effects of average precipitate microstructure on lifetimes were not clearly delineated, one sample showed an anomalously high number of the smallest size (30 nm to 50 nm) Ag3Sn precipitates, and this sample also exhibited a much longer lifetime than all the other samples. Thus, some evidence was presented that samples of particular orientations and precipitate microstructures can exhibit anomalous fatigue lifetimes.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Similar content being viewed by others

References

  1. P. Borgesen, T. Bieler, L. Lehman, and E. Cotts, MRS Bull. 32, 360 (2007).

    Google Scholar 

  2. Y. Xing, J. Electron. Mater. (submitted)

  3. Y. Kariya, T. Hosoi, S. Terashima, M. Tanaka, and M. Otsuka, J. Electron. Mater. 33, 321 (2004).

    Article  CAS  ADS  Google Scholar 

  4. K.S. Kim, S.H. Huh, and K. Suganuma, Mater. Sci. Eng. A 333, 106 (2002).

    Article  Google Scholar 

  5. F. Ochoa, X. Deng, and N. Chawla, J. Electron. Mater. 33, 1596 (2004).

    Article  CAS  ADS  Google Scholar 

  6. M. Kerr and N. Chawla, Acta Mater. 52, 4527 (2004).

    Article  CAS  Google Scholar 

  7. F. Ochoa, J.J. Williams, and N. Chawla, J. Electron. Mater. 32, 1414 (2003).

    Article  CAS  ADS  Google Scholar 

  8. P.W. Bridgman, Proc. Am. Acad. Arts Sci. 60, 305 (1925).

    Google Scholar 

  9. J.A. Rayne and B.S. Chandrasekhar, Phys. Rev. 120, 1658 (1960).

    Article  CAS  ADS  Google Scholar 

  10. F. Yang and J.C.M. Li, J. Mater. Sci. Mater. Electron. 18, 191 (2007).

    Article  CAS  Google Scholar 

  11. A.U. Telang and T.R. Bieler, Solid State Phenom. 105, 219 (2005).

    Article  CAS  Google Scholar 

  12. A.U. Telang, T.R. Bieler, and M.A. Crimp, Mater. Sci. Eng. A 421, 22 (2006).

    Article  Google Scholar 

  13. T.R. Bieler, H. Jiang, L.P. Lehman, T. Kirkpatrick, and E.J. Cotts, 56th IEEE Transactions on Components and Packaging Technology, vol. 31 (2006), 370 pp

  14. S. Park, R. Dhakal, L. Lehman, and E. Cotts, Acta Mater. 55, 3253 (2007).

    Article  CAS  Google Scholar 

  15. B. Arfaei, Y. Xing, J. Woods, J. Wolcotts, P. Tumne, P. Borgesen, and E. Cotts, 58th Electronic Components and Technology Conference (2008), 459 pp

  16. T.M.K. Korhonen, L. Lehman, M.A. Korhonen, and D.W. Henderson, J. Electron. Mater. 36, 173 (2007).

    Article  CAS  ADS  Google Scholar 

Download references

Acknowledgement

We acknowledge Dr. Larry Lehman from S3IP lab in Binghamton University for important discussions.

Author information

Authors and Affiliations

  1. Physics and Materials Science, Binghamton University, PO Box 6000, Binghamton, NY, 13902, USA

    Babak Arfaei & Eric Cotts

Authors
  1. Babak Arfaei
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. Eric Cotts
    View author publications

    You can also search for this author in PubMed Google Scholar

Corresponding author

Correspondence to Eric Cotts.

Rights and permissions

Reprints and permissions

About this article

Cite this article

Arfaei, B., Cotts, E. Correlations Between the Microstructure and Fatigue Life of Near-Eutectic Sn-Ag-Cu Pb-Free Solders. J. Electron. Mater. 38, 2617–2627 (2009). https://doi.org/10.1007/s11664-009-0932-y

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s11664-009-0932-y

Keywords

Search

Navigation