Effects of Minor Additions of Zn on Interfacial Reactions of Sn-Ag-Cu and Sn-Cu Solders with Various Cu Substrates during Thermal Aging

  • Published:
Journal of Electronic Materials Aims and scope Submit manuscript

Abstract

The effects of Zn additions to Sn-0.7Cu and Sn-3.8Ag-0.7Cu (all in wt.% unless specified otherwise) Pb-free solders on the interfacial reactions with Cu substrates were investigated. The study was focused on the intermetallic compound (IMC) growth, Cu consumption and void formation as a function of thermal aging and solder composition. Four different kinds of Cu substrates (high-purity Cu, oxygen-free Cu, vacuum-sputtered Cu, and electroplated Cu) were prepared to compare their interfacial reaction behaviors with Zn-added solders. Thermal aging was performed at 150°C for up to 1000 h to accelerate the interfacial reactions between solders and Cu substrates. Growth of IMCs (Cu6Sn5 and Cu3Sn) in Zn-added solders was slower than those without Zn additions. The growth of the Cu3Sn phase, in particular, was drastically reduced in the Zn-added solders on all four Cu substrates. On an electroplated Cu substrate, numerous voids were observed in the Cu3Sn phase for Sn-Cu and Sn-Ag-Cu solders aged at 150°C for 1000 h. However, these voids were largely eliminated in the Zn-added solders. On the other three Cu substrates, the conditions which produce a high density of voids were not found after aging both solders with and without Zn. The Cu consumption with Zn-added solders was also significantly lower. The beneficial effects of Zn additions on interfacial reaction behaviors are reported, and the corresponding mechanisms in suppressing void formation and Cu consumption due to Zn additions will be discussed.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Similar content being viewed by others

References

  1. J. Bath, C. Handwerker, and E. Bradley, Circ. Assemb. 11, 45 (2000)

    Google Scholar 

  2. I.E. Anderson, J.C. Foley, B.A. Cook, J. Harringa, R.K. Terpatra, and O. Unal, J. Electron. Mater. 29, 1050 (2001)

    Article  Google Scholar 

  3. K.J. Puttlitz, Handbook of Lead-Free Solder Technology for Microelectronic Assemblies, ed. K.J. Puttlitz and K.A. Stalter (New York: Marcel Dekker, Inc., 2004), pp. 239–280

    Google Scholar 

  4. S.K. Kang, Handbook of Lead-Free Solder Technology for Microelectronic Assemblies, ed. K.J. Puttlitz and K.A. Stalter (New York: Marcel Dekker, Inc., 2004), pp. 281–300

    Google Scholar 

  5. T.C. Chiu, K. Zeng, R. Stierman, D. Edwards, and K. Ano, Proceedings of 54th Electronic Components and Technology Conference (Piscataway, NJ: IEEE, 2004), pp. 1256–1262

    Google Scholar 

  6. M. Date, T. Shoji, M. Fujiyoshi, K. Sato, and K.N. Tu, Proceedings of 54th Electronic Components and Technology Conference (Piscataway, NJ: IEEE, 2004), pp. 668–674

    Google Scholar 

  7. L.P. Lehman, R.K. Kinyanjui, L. Zavalij, A. Zribi, and E.J. Cotts, Proceedings of 53rd Electronic Components and Technology Conference (Piscataway, NJ: IEEE, 2003), pp. 1215–1221

    Book  Google Scholar 

  8. R. Kinyanjui, L.P. Lehman, L. Zavalij, and E. Cotts, J. Mat. Res. 20(11), 2914 (2005)

    Article  CAS  Google Scholar 

  9. K.S. Kim, S.H. Huh, and K. Suganuma,Microelectron. Reliab. 43, 259 (2002)

    Google Scholar 

  10. M.J. Rizvi, Y.C. Chan, C. Bailey, H. Lu, and M.N. Islam, J. Alloys Compd. 407, 208 (2006)

    Article  CAS  Google Scholar 

  11. G.Y. Li, B.L. Chen, and J.N. Tey, IEEE Trans. Electron. Packag. Manuf. 27(1), 77 (2004)

    Article  CAS  Google Scholar 

  12. S.K. Kang, D.-Y. Shih, D. Leonard, D.W. Henderson, T. Gosselin, S.-I. Cho, J. Yu, and W.K. Choi, JOM 56(6), 34 (2004)

    Article  CAS  Google Scholar 

  13. S.K. Kang, D. Leonard, D.-Y. Shih, L. Gignac, D.W. Henderson, S.-I. Cho, and J. Yu, J. Electron. Mater. 35(3), 479 (2006)

    Article  CAS  Google Scholar 

  14. I. De Sousa, D.W. Henderson, L. Patry, S.K. Kang, and D.-Y. Shih, Proceedings of 56th Electronic Components and Technology Conference (Piscataway, NJ: IEEE, 2006), pp. 1454–1462

    Book  Google Scholar 

  15. L. Huang, Q. Wang, and J. Ma, Proceedings of 2000 International Symposium on Electronic Materials & Packaging, pp 191–193

  16. B. Sundman, B. Jansson, J.O. Andersson, CALPHAD 9, 153 (1985)

    Article  CAS  Google Scholar 

  17. A.P. Miodownik, Phase Diagrams of Binary Copper Alloys, ed. P.R. Subramanian and D.E. Laughlin (Materials Park, OH: ASM International, 1994), pp. 487–496

  18. V. Voort, Metallography Principles and Practice, (New York: McGraw-Hill, 1984), pp 625

    Google Scholar 

  19. K.N. Tu and R.D. Thompson, Acta Metall. 30, 947 (1982)

    Article  CAS  Google Scholar 

  20. K.F. Dreyer, W.K. Neils, R.R. Chromik, D. Grosman, and E.J. Cotts, Appl. Phys. Lett. 67(19), 2795 (1995)

    Article  CAS  Google Scholar 

  21. J.H. Shim, C.S. Oh, B.J. Lee, and D.N. Lee, Z. Metallkd 87(3), 205 (1996)

    CAS  Google Scholar 

  22. T. Jantzen and P.J. Spencer, CALPHAD 22, 417 (1998)

    Article  CAS  Google Scholar 

  23. L. Xu and John H.L. Pang, Proceedings of 56th Electronic Components and Technology Conference (Piscataway, NJ: IEEE, 2006), pp. 275–282

    Google Scholar 

  24. D.W. Henderson, P. Borgesen, P. Kondos, I. De Sousa, L. Patry, and L. Yin, Lead-free Technology Workshop on “What The Electronics Industry Missed For 80 Years...Interfacial Void Formation In Solder Joints With Cu Pad Structures During Thermal Aging”, 2006 TMS Annual Meeting, 3/13-15/2006, San Antonio, TX

  25. I.E. Anderson and J.L. Harringa, J. Electron. Mater. 33(12), 1485 (2004)

    Article  CAS  Google Scholar 

Download references

Author information

Authors and Affiliations

Authors

Corresponding author

Correspondence to Hyuck Mo Lee.

Rights and permissions

Reprints and permissions

About this article

Cite this article

Cho, M., Kang, S., Shih, DY. et al. Effects of Minor Additions of Zn on Interfacial Reactions of Sn-Ag-Cu and Sn-Cu Solders with Various Cu Substrates during Thermal Aging. J. Electron. Mater. 36, 1501–1509 (2007). https://doi.org/10.1007/s11664-007-0254-x

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s11664-007-0254-x

Keywords

Navigation