Abstract
The effect of Al2O3 and CaO/SiO2 on the viscosity of the CaO-SiO2-10 mass pct MgO-Al2O3 slags was studied at fully liquid temperatures of 1773 K (1500 °C) and below. At fixed CaO/SiO2 between 0.8 and 1.3, higher Al2O3 content increased the slag viscosity due to the polymerization of the aluminate structures. At fixed Al2O3 of 15 and 20 mass pct, increasing the CaO/SiO2 from 0.8 to 1.3 resulted in lower viscosity due to the depolymerization of the aluminate structure.
Similar content being viewed by others
References
J. Muller and M. Erwee: Southern African Pyrometallurgy 2011, R.T. Jones and P. den Hoed, eds., SAIMM, Johannesburg, South Africa, 2011.
A. Kondratiev, E. Jak, and P.C. Hayes: JOM, 2002, vol. 54, no. 11, pp. 41–45.
A. Shankar, M. Görnerup, A.K. Lahiri, and S. Seetharaman: Metall. Mater. Trans. B, 2007, vol. 38B, no. 6, pp. 911–15.
M.M. Gladkii: Metallurgist, 1961, vol. 5, no. 8, pp. 355–57.
Y. Morizane, B. Ozturk, and R.J. Fruehan: Metall. Mater. Trans. B, 1999, vol. 30B, pp. 29–43.
J.S. Machin and D.L. Hanna: J. Am. Ceram. Soc., 1945, vol. 28, no. 11, pp. 310–16.
Y.S. Lee, D.J. Min, S.M. Jung, and S.H. Yi: ISIJ Int., 2004, vol. 44, no. 8, pp. 1283–90.
J.H. Park, D.J. Min, and H.S. Song: Metall. Mater. Trans. B, 2004, vol. 35B, pp. 269–75.
K. Ishii and Y. Kashiwaya: Advanced Pulverized Coal Injection Technology and Blast Furnace Operation, K. Ishii, ed., Pergamon, Oxford, U.K., 2000, pp. 133–66.
W.H. Kim, I. Sohn, and D.J. Min: Steel Res. Int., 2010, vol. 81, no. 9, pp. 735–41.
T. Iida, H. Sakai, Y. Kita, and K. Shigeno: ISIJ Int., 2000, vol. 40, pp. S110–14.
P.V. Riboud, Y. Roux, L.D. Lucas, and H. Gaye: Fachber. Huttenprax. Metal., 1981, vol. 19, pp. 859–60.
K.C. Mills and S. Sridhar: Ironmaking Steelmaking, 1999, vol. 26, pp. 262–8.
A.B. Fox: Ph.D. Thesis, Imperial College, London, U.K., 1999.
G. Urbain: Trans. J. Br. Ceram. Soc., 1981, vol. 80, pp. 139–41.
G. Urbain: Steel Res. Int., 1987, vol. 58, pp. 111–6.
I. Sohn and D.J. Min: Steel Res. Int., 2012, vol. 83, pp. 611–30.
M. Kowalski, P.J. Spencer, and D. Neuschütz: Slag Atlas, 2nd ed., Ed. Verein Deutscher Eisenhüttenleute, Verlag Stahleisen GmbH, Düsseldorf, Germany, 1995, pp. 160.
G.H. Kim and I. Sohn: Metall. Mater. Trans. B, 2011, vol. 42B, no. 6, pp. 1218–23.
H.-S. Park, S.S. Park, and I. Sohn: Metall. Mater. Trans. B, 2011, vol. 42B, no. 6, pp.1218–23.
K.C. Mills: Slag Atlas, 2nd ed., Ed. Verein Deutscher Eisenhüttenleute, Verlag Stahleisen GmbH, Düsseldorf, Germany, 1995, pp. 350.
W. Wang and A. Cramb: Steel Res. Int., 2008, vol. 79, pp. 271–77.
H.-S. Park, H. Kim, and I. Sohn: Metall. Mater. Trans. B, 2011, vol. 42B, pp. 324–30.
G.H. Kim and I. Sohn: ISIJ Int., 2012, vol. 52, no. 1, pp. 68–73.
J.H. Park, D.J. Min, and H.S. Song: ISIJ Int., 2002, vol. 42, pp. 344–51.
J.H. Park, H. Kim, and D.J. Min: Metall. Mater. Trans. B, 2008, vol. 39B, no. 1, pp. 150–3.
P.F. McMillan: Am. Mineral., 1984, vol. 69, pp.645–59.
B.O. Mysen: Earth-Sci. Rev., 1990, vol. 27, pp. 281–365.
A. Burns, H.P. Brack, and W.M. Risen Jr.: J. Non-Cryst. Sol., 1991, vol. 131, pp. 994–1000.
B.O. Mysen, D. Virgo, and C.M. Scarfe: Am. Mineral., 1980, vol. 65, pp. 690–710.
P.F. McMillan, B.T. Poe, PH. Gillet, and B. Reynard: Geochim. Cosmochim. Acta, 1994, vol. 58, no. 17, pp. 3653–64.
This study was partially supported by the Brain Korea 21 (BK21) Project at the Division of the Humantronics Information Materials and the National Science Foundation of Korea Project No.2010-8-2150 and 2011-8-0738.
Author information
Authors and Affiliations
Corresponding author
Additional information
Manuscript submitted May 13, 2012.
Rights and permissions
About this article
Cite this article
Kim, H., Matsuura, H., Tsukihashi, F. et al. Effect of Al2O3 and CaO/SiO2 on the Viscosity of Calcium-Silicate–Based Slags Containing 10 Mass Pct MgO. Metall Mater Trans B 44, 5–12 (2013). https://doi.org/10.1007/s11663-012-9759-7
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11663-012-9759-7