Abstract
The existing forms of N and Al in HSLC (high strength low carbon) steel produced by TSCR (thin slab casting and rolling process), the precipitation thermodynamics and kinetics of AlN, and its effects on structure and mechanical property are studied. The experimental results show that only a small quantity of nitrogen is combined into AlN in HSLC steel produced by TSCR and most of the nitrogen in steel is still free nitrogen. Aluminum-nitride is mainly precipitated during the period of slow air cooling after coiling, but not during rolling and water cooling. The acid-soluble aluminum has no obvious effect on the grain size and mechanical property of HSLC steel produced by TSCR whose acid-soluble aluminum content is 0.005%–0.043%. The precipitation of AlN is not the main cause of grain refinement of HSLC steel produced by TSCR, nor is AlN the dominating precipitate that has precipitation strengthening effect. The nano nitrides are not pure AlN, but have complex compositions.
Similar content being viewed by others
References
Morrison W B. Nitrogen in the steel product. Ironmaking and Steelmaking, 1989, 16(2): 123–128
Michel J P, Jonas J J. Precipitation kinetics and solute strengthening in high temperature austenites containing Al and N. Acta Metallurgica, 1981, 29: 513–526
Kiichi Narita. Physical chemistry of the groups IVa(Ti, Zr), Va(V, Nb, Ta) and the rare earth elements in steel. Trans ISIJ, 1975, 15: 145–152
Irvine K J, Pickering F B, Gladman T. Grain-refined C-Mn steels. J Iron and Steel Institute, 1967, 161–182
Erasmus L A. Effect of aluminum additions on forgeability, austenite grain coarsening temperature, and impact properties of steel. J Iron and Steel Institute, 1964, 32–41
Gladman T, Pickering F B. Grain-coarsening of austenite. J Iron and Steel Institute, 1967, 653–664
Kang Y L, Yu H, Fu J, et al. Morphology and precipitation kinetics of AlN in hot strip of low carbon steel produced by compact strip production. Mater Sci Eng A, 2003, 351(1–2): 265–271
Yong Q L. The Second Phase in Iron and Steel Materials (in Chinese). Beijing: Metallurgical Industry Press, 2006
Fu J, Wu H J, Liu Y C, et al. Nano-scaled iron-carbon precipitates in HSLC and HSLA steels. Sci China Ser E-Tech Sci, 2007, 50(2): 166–176
Author information
Authors and Affiliations
Corresponding author
Additional information
Supported by the National Natural Science Foundation of China (Grant No. 50334010) and the State Foundation for Key Projects: New Generation of Steels (Grant No. G1998061500)
Rights and permissions
About this article
Cite this article
Fu, J., Liu, Y. & Wu, H. The precipitation and effect of nano nitrides in HSLC steel. Sci. China Ser. E-Technol. Sci. 51, 989–998 (2008). https://doi.org/10.1007/s11431-008-0059-z
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11431-008-0059-z