Abstract
In this paper, we report on the TL glow curves and kinetic parameters, activation energy, order of kinetics, and the frequency factor of copper-doped zinc sulfide nanophosphor under UV irradiations. The sample was prepared by the chemical precipitation method; thereafter, the TL glow curves were recorded for different doses of UV exposure at a heating rate of 10 °C/s. The synthesized nanophosphor exhibited TL glow peaks at 241, 255, and 281 °C for the heating rate 10 °C/s at different doses of 5, 10, and 15 min of UV exposure. The kinetic parameters activation energy E, the order of kinetics b, and the frequency factor S of synthesized nanophosphor of ZnS:Cu have been calculated by using a peak shape method while the trap depth was determined using different formulae. The sample was characterized by XRD (X-ray diffraction) and SEM (scanning electron microscope).
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs11164-012-0905-2/MediaObjects/11164_2012_905_Fig1_HTML.gif)
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs11164-012-0905-2/MediaObjects/11164_2012_905_Fig2_HTML.jpg)
![](http://media.springernature.com/m312/springer-static/image/art%3A10.1007%2Fs11164-012-0905-2/MediaObjects/11164_2012_905_Fig3_HTML.gif)
Similar content being viewed by others
References
W.Q. Peng, G.W. Cong, S.C. Qu, Z.G. Wang, Opt. Mater. 29, 313 (2006)
C. Bouvy, F. Piret, W. Marine, B.L. Su, Chem. Phys. Lett. 433, 350 (2007)
B. O Reagan, M Gratzel, Nature 353, 737 (1991)
G.M. Pankonk, Appl. Catal. 72, 217 (1991)
S. Lazarouk et al., Appl. Phys. Lett. 68, 1646 (1996)
R.N. Bhargava, D. Gallagher, X. Hong, A. Nurmikko, Phys. Rev. Lett. 72, 416 (1994)
E.H. Nicolian, R. Tsu, J. Appl. Phys. 74, 4020 (1993)
S. Schmitt-Rink, D.A.B. Miller, D.S. Chemla, Phys. Rev. B 35, 8113 (1987)
V. Nogriya, J.K. Dingre, M. Ramrakhiani, B.P., Chandra Chalcogenide Lett. vol.5, No. 12, (2008), pp 365–373
L.S. Dong, X.F. Fu, M.W. Wang, C.H. Liu, J. Lumin. 87–89, 538 (2000)
N. Francois, B. Ginzberg, S.A. Bilmes, J. Sol-Gel. Sci. Technol. 13, 314 (1998)
R. Premachandran, S. Banerjee, V.T. Jhon, G.L. Mcpherson, J.A. Akkara, D.L. Kaplan, Chem. Mater. 9, 1342 (1997)
M.Y. Gao, X. Zhang, B. Yang, F. Li, J.C. Shen, Thin Solid Films, 242, 283 (1996)
R. Chen, Analysis of thermally stimulated processes (Pergamon Press, Newyork, 1981)
G. Kitis, C. Furetta, M. Prokic et al., J. Phys. D Appl. Phys. 33, 1252 (2000)
D. Vikas, N.S. Suryanarayana, K. Jagjeet, J. Miner. Mater. Charact. Eng. 9(12), 1101 (2010)
J.T. Randall, M.H.F. Wilkins, Proc. R. Soc. A 184, 366 (1945)
F. Urbach, Ber. Winer IIa 139, 363 (1930)
L.I. Lushihik, Soviet Phys. JETP, 3 390 (1956)
R. Chen, J. Electrochem. Soc. 116, 1254 (1969)
K. Jagjeet,D. Vikas, N.S. Suryanarayana, A. Sadhana, S.J. Dhoble, Int. J. Nanotechnol. Appl. 6(2), 99 (2012)
Acknowledgments
We are grateful to UGC for funding through a Minor Research Project. The XRD part of the paper is related to IUC Indore, and we are grateful to Dr. Mukul Gupta for his support.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Kaur, J., Dubey, V., Suryanarayana, N.S. et al. Thermoluminescence study of ZnS:Cu nanoparticles. Res Chem Intermed 39, 3895–3900 (2013). https://doi.org/10.1007/s11164-012-0905-2
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11164-012-0905-2