Abstract
A novel and effective method was developed for raw silk fabric degumming with the application of low-pressure argon plasma in pretreatment combining a subsequent one-step mild wet-chemical process. The plasma parameters, such as argon pressure, discharge power and exposure time, were optimized according to degumming loss and the properties of fabric such as capillary rise, tensile strength, bending rigidity, etc. An optimized plasma pretreatment for raw silk fabric degumming was at 80 Pa of argon gas and 60 W glow discharge power for 5–10 min. The raw silk fabric and fibers pretreated by argon plasma were characterized by scanning electronic microscopy and X-ray powder diffraction. In comparison with a conventional degumming process, the proposed method achieved comparable degumming efficiency and properties of silk fabric, and it was more environmentally friendly by shortening the conventional wet-chemical treatment process, saving the dosage of degumming agents, water and energy.
Similar content being viewed by others
References
Freddi G, Mossotti R, Innocenti R (2003) J Biotechnol 106:101
Yamada H, Nakao H, Takasu Y et al (2003) Mater Sci Eng Crystallogr 14:41
Komatsu K (2003) The formation and structure of silk. In: Hojo N (ed) Chemical and structural characteristics of silk sericin. Shinkyo printing, Nagano, pp 379–415
Wu ZY, Feng ZZ et al (eds) (1992) Silk reeling chemistry, 2nd edn. Textile industrial, Beijing, pp 94–114
Jiang P, Liu H, Wang C et al (2006) Mater Lett 60:919
Li R, Ye L, Mai YW (1997) Composites Part A Appl Sci Manu 28:73
Vohrer U, Müller H, Oehr C (1998) Surf Coat Technol 98:1128
Borcia G, Anderson CA, Brown NMD (2006) Surf Coat Technol 201:3074
Yip J, Chan K, Sin KM et al (2002) J Mater Process Technol 123:5
Vallon S, Drévillon B, Poncin-Epaillard F (1997) Appl Surf Sci 108:177
Wertheimer MR, Fozza AC, Holländer A (1999) Nucl Instrum Method Phys Res Sect B Beam Interact Mater Atom 151:65
Yuan LY, Chen CS, Shyu SS et al (1992) Composite Sci Technol 45:1
Anand M, Cohen RE, Baddour RF (1981) Polymer 22:361
Smiley RJ, Delgass WN (1993) J Mater Sci 28:3601
Jeong BY, Hwang MS, Lee C et al (2001) Surf Coat Technol 135:279
Chaivan P, Pasaja N, Boonyawan D et al (2005) Surf Coat Technol 193:356
Canal C, Gaboriau F, Molina R et al (2007) Plasma Process Polym 4:445
Matthews SR, McCord MG, Bourham MA (2005) Plasma Process Polym 2:702
De Geyter N, Morent R, Leys C (2006) Surf Coat Technol 201:2460
Poll HU, Schladitz U, Schreiter S (2001) Surf Coat Technol 142–144:489
Wang CX, Ren Y, Qiu YP (2007) Surf Coat Technol 202:77
Ferrero F (2003) Polymer Test 22:571
Raffaele-Addamo A, Riccardi C, Selli E, Barni R et al (2003) Surf Coat Technol 174–175:886
Garg S, Hurren C, Kaynak A (2007) Synthetic Met 157:41
Hossain MM, Herrmann AS, Hegemann D (2007) Plasma Process Polym 4:1068
Hossain MM, Hegemann D, Fortunato G et al (2007) Plasma Process Polym 4:471
Hossain MM, Herrmann AS, Hegemann D (2007) Plasma Process Polym 4:135
Hossain MM, Herrmann AS, Hegemann D (2006) Plasma Process Polym 3:299
Osenberg F, Theirich D, Decker A et al (1999) Surf Coat Technol 116–119:808
Canal C, Gaboriau F, Ricard A et al (2007) Plasma Chem Plasma Process 27:404
Wong KK (2000) Text Res J 70:886
Da Y, Griesser HJ, Mau AWH et al (1991) Polymer 32:1126
Shahidi S, Ghoranneviss M, Moazzenchi B et al (2007) Plasma Process Polym 4:1098
Castelvetro V, Fatarea E, Corsi L et al (2005) Plasma Process Polym 3:48
Demura M, Takekawa T, Asakura T et al (1992) Biomaterials 13:276
Liu YC, Lu DN (2006) Plasma Chem Plasma Process 26:119
Bhat NV, Upadhyay DJ (2003) Plasma Chem Plasma Process 23:389
Textiles-Capillary rise measurement method—strip method (1999) In: China textile criteria of FZ/T01071-1999, Criteria Press of China, Beijing
Textiles-Tensile properties of fabrics—Part 1: determination of breaking force and elongation at breaking force—strip method (1997) In: China textile criteria of GB/T3923.1-1997, Criteria Press of China, Beijing
Textiles-Determination of bending length of fabrics (2001) In: China textile criteria of GB/T 1838-2001, Criteria Press of China, Beijing
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Long, JJ., Wang, HW., Lu, TQ. et al. Application of Low-Pressure Plasma Pretreatment in Silk Fabric Degumming Process. Plasma Chem Plasma Process 28, 701–713 (2008). https://doi.org/10.1007/s11090-008-9153-z
Received:
Revised:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11090-008-9153-z