Abstract
A shape memory polymer wire for orthodontic application was prepared by melt-spinning of polyurethane block copolymer (PU) which was synthesized in a two-step process from a reaction of 4,4′-methylene bis(phenylisocyanate), poly(ε-caprolactone)diol (PCL), and 1,4-butanediol. An orthodontic test using the PU wire was carried out in an orthodontic model with a metal bracket. High shape recovery force of 70 gf for PU wire at 40 wt% hard segment content could be preserved for even 1 month after a shape recovery force test at a constant temperature of 50°C. The shape recovery force decreased exponentially during the initial 2 h, but reached an equilibrium shape recovery force of 50 gf after about 20 days. It was found that this shape recovery force was sufficient to correct misaligned teeth in the orthodontic test. The shape memory PU wire possesses strong potential as a novel orthodontic appliance with esthetically appealing appearance.
Similar content being viewed by others
References
L.E. Medawar, P. Rocher, J.C. Hornez, M. Traisnel, J. Breme, H.F. Hildebrand, Biomol. Eng. 19, 153 (2002). doi:10.1016/S1389-0344(02)00041-2
I. Kocaderli, S. Canay, K. Akca, Am. J. Orthod. Dentofac. Orthod. 119, 617 (2001). doi:10.1067/mod.2001.113655
R.G. Alkire, M.D. Bagby, M.A. Gladwin, H. Kim, Dent. Mater. 13, 2 (1997). doi:10.1016/S0109-5641(97)80001-2
W.S. Mullins, M.D. Bagby, T.L. Norman, Dent. Mater. 12, 308 (1996). doi:10.1016/S0109-5641(96)80039-X
G.V. Newman, Prog. Rep. Am. J. Orthod. 51, 901 (1965). doi:10.1016/0002-9416(65)90203-4
M.D. Rains, S.J. Chaconas, A.A. Caputo, R. Rand, J. Clin. Orthod. 11, 120 (1977)
K. Fujihara, K. Teo, R. Gopal, P.L. Loh, V.K. Ganesh, S. Ramakrishna et al., Compos. Sci. Technol. 64, 775 (2004). doi:10.1016/j.compscitech.2003.09.012
Z.M. Huang, R. Gopal, K. Fujihara, S. Ramakrishna, P.L. Loh, W.C. Foong et al., Biomaterials 24, 2941 (2003). doi:10.1016/S0142-9612(03)00093-0
A. Valiathan, S. Dhar, Trends Biomater. Artif. Organs 20, 16 (2006)
T. Imai, F. Watari, S. Yamagata, M. Kobayashi, K. Nagayama, Y. Toyoizumi et al., Biomaterials 19, 2195 (1998). doi:10.1016/S0142-9612(98)00127-6
N. Moszner, U. Salz, Prog. Polym. Sci. 26, 535 (2001). doi:10.1016/S0079-6700(01)00005-3
B.S. Lee, B.C. Chun, Y.C. Chung, K.I. Sul, J.W. Cho, Macromolecules 34, 6341 (2001)
F.E. Feninat, G. Laroche, M. Fiset, D. Mantovani, Adv. Eng. Mater. 4, 91 (2002). doi :10.1002/1527-2648(200203)4:3<91::AID-ADEM91>3.0.CO;2-B
K. Gorna, S. Gogolewski, Polym. Degrad. Stabil. 79, 465 (2003). doi:10.1016/S0141-3910(02)00362-2
A. Lendlein, S. Kelch, Angew. Chem. Int. Ed. 41, 2034 (2002). doi :10.1002/1521-3773(20020617)41:12<2034::AID-ANIE2034>3.0.CO;2-M
F. Yeh, B.S. Hsiao, Macromolecules 36, 1940 (2003). doi:10.1021/ma0214456
Y.C. Jung, H.H. So, J.W. Cho, J. Macromol. Sci. Part B Phys. 45, 453 (2006). doi:10.1080/00222340600767513
M. Watanabe, N. Wakimoto, T. Hirai, M. Yokoyama, J. Appl. Polym. Sci. 95, 1566 (2005). doi:10.1002/app.21365
Acknowledgment
This work was supported by the SRC/ERC Program of MOST/KOSEF (R11-2005-065).
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Jung, Y.C., Cho, J.W. Application of shape memory polyurethane in orthodontic. J Mater Sci: Mater Med 21, 2881–2886 (2010). https://doi.org/10.1007/s10856-008-3538-7
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10856-008-3538-7