Abstract
Superconducting Bi–Pb–Sr–Ca–Cu–O (BPSCCO) thin films were grown on MgO substrates by a spray pyrolysis technique, followed by a solid-state reaction. The thin films with nominal composition Bi1.65Pb0.4Sr1.2Ca1.2Cu2.5(NO3)δ were grown varying mainly the annealing temperature between 835 and 855 °C in order to observe the influence on the critical temperature Tc. At 855 °C the higher Tc was obtained for the 2212 phase. The thin films were then analyzed by X-ray diffraction, R-T measurements and atomic absorption spectroscopy.
Similar content being viewed by others
References
H. Maeda, Y. Tanaka, M. Fukutomi, T. Asano, Jpn. J. Appl. Phys. 27, L209–L210 (1988)
E. Díaz-valdés, G. Pacheco-Malagón, G. Contreras-Puente, C. Mejía-García, G. Andrade-Garay, J. Ortiz-López, A. Conde-Gallardo, C. Falcony, Mater. Chem. Phys. 36, 64–67 (1993)
K.C. Hewitt, X.K. Chen, X. Meng-Burany, A.E. Curzon, J.C. Irwin, Physica C 251, 192–204 (1995)
C. Mejía-García, E. Díaz-Valdés, G. Contreras-Puente, J.L. López-López, M. Jergel, A. Morales, Physica C 416, 11–16 (2004)
Y. Yu, X. Jin, D.X. Cai, X.X. Yao, C. Hu, K.Y. Ding, D. Feng, Phys. Status Solidi, A 146, K33–K36 (1994)
S. Rahier, S. Stassen, R. Cloots, M. Ausloos, Mater. Lett. 60, 298–300 (2006)
S.M. Khalil, A. Sedky, Physica B 357, 299–304 (2005)
E. Díaz-Valdés, M. Jergel, C. Falcony-Guajardo, F. Morales, J. Araujo-Osorio, Thin Solid Films 373, 122–128 (2000)
Internacional Centre for Diffraction Data, Item 49–735 in PC Powder Diffraction File WIN, V 2.2
J.M. Tarascon, W.R. Mckinnon, P. Barboux, D.M. Hwang, B.G. Bagley, L.H. Greene, G.W. Hull, Y. Lepage, N. Stoffel, M. Giroud, Phys. Rev. B 38, 8885–8892 (1988)
Acknowledgement
The authors would like to thank to Dr. Jaime Ortiz (ESFM-IPN, Mexico) for reading the manuscript.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Díaz-Valdés, E., Mejía-García, C., López-López, J.L. et al. Influence of annealing on the critical temperature of Bi–Pb–Sr–Ca–Cu–O thin films. J Mater Sci: Mater Electron 18, 1167–1170 (2007). https://doi.org/10.1007/s10854-007-9286-5
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10854-007-9286-5