Abstract
X-ray photoelectron spectroscopy (XPS) was used to examine the NO2 adsorption behaviour on the LaFeO3 and Pt electrodes of planar yttria stabilized zirconia non-Nernstian gas sensors. The electrochemical sensors were exposed to the same gas atmosphere containing 1000 ppm NO2 at 650°C. XPS of the as-prepared sensors and sensors after exposure to NO2 revealed bonded nitrogen peaks on the surface of the semiconducting oxide but no nitrogen peaks on the Pt electrode. Therefore, NO2 adsorption on a LaFeO3 electrode plays an important role in the NO2 detection mechanism.
Similar content being viewed by others
References
N. Miura, H. Kurosawa, M. Hasei, G. Lu, N. Yamazoe, Solid State Ionics 86–88, 1069–1073 (1996)
N. Miura, N. Yamazoe, Approch to high-performance electrochemical NOx sensors based on solid electrolytes, in Sensors Update, Vol. 6, ed. by H. Baltes, W. Göpel, J. Hesse (Wiley-VCH, Weinheim, 2000), pp. 191–210
N. Miura, S. Zhuiykov, T. Ono, M. Hasei, N. Yamazoe, Sens. Actuators B 83, 222–229 (2002)
T. Hibino, A. Hashimoto, S. Kakimoto, M. Sano, J. Electrochem. Soc. 148, H1–H5 (2001)
E.L. Brosha, R. Mukundan, D.R. Brown, F.H. Garzon, J.H. Visser, M. Zanini, Z. Zhou, E.M. Logothetis, Sens. Actuators B 69, 171–182 (2000)
E.L. Brosha, R. Mukundan, D.R. Brown, F.H. Garzon, J.H. Visser, Solid State Ionics 148, 61–69 (2002)
L. Chevallier, E.D. Bartolomeo, M.L. Grilli, M. Mainas, B.M. White, E.D. Wachsman, E. Traversa, Non-nernstian planar sensors based on YSZ with an Nb2O5 electrode: discussion on sensing mechanism, in: E. Wachsman, V. Briss, F. Garzon, R. Mukundan, E. Traversa (Eds.), State Ionic Devices IV, Vol 1 (7), The Electrochemical Soc. Trans., pp. 163–171 (2005)
J.W. Yoon, M.L. Grilli, E. Di Bartolomeo, R. Polini, E. Traversa, Sens. Actuators B 76, 483–488 (2001)
M.L. Grilli, E. Di Bartolomeo, E. Traversa, J. Electrochem. Soc. 148(9), H98–H102 (2001)
M.L. Grilli, N. Kaabbuathong, A. Dutta, E. Di Bartolomeo, E. Traversa, J. Ceram. Soc. Jpn. 110(3), 159–162 (2002)
E. Di Bartolomeo, M.L. Grilli, E. Traversa, J. Electrochem. Soc. 151(5), H133–H139 (2004)
E. Di Bartolomeo, N. Kaabbuathong, A. D’Epifanio, M.L. Grilli, E. Traversa, H. Aono, Y. Sadaoka, J. Euro. Ceram. Soc. 24, 1187–1190 (2004)
E. Traversa, M. Sakamoto, Y. Sadaoka, J. Am. Ceram. Soc. 79, 1401–1404 (1996)
E. Di Bartolomeo, M.L. Grilli, N. Kaabbuathong, E. Traversa, Solid State Ionics 173, 173–181 (2004)
N. Miura, H. Kurosawa, M. Hasei, G. Lu, N. Yamazoe, Solid State Ionics 86–88, 1069–1073 (1996)
G. Lu, N. Miura, N. Yamazoe, J. Mater. Chem. 7(8), 1445–1449 (1997)
N. Miura, G. Lu, M. Ono, N. Yamazoe, Solid State Ionics 117, 283–290 (1998)
Handbook of X-ray Photoelectron Spectroscopy, J. F. Moulder, W. F. Stickle, P. E. Sobol, K. D. Bomben, and J. Chastain, Editors, Eden Prairie, MN (1992)
E. Traversa, S. Villanti, G. Gusmano, H. Aono, Y. Sadaoka, J. Am. Ceram. Soc. 82, 2442–2450 (1999)
Acknowledgments
The present research was conducted by the research fund of Dankook University in 2009.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Yoon, JW., Di Bartolomeo, E. & Traversa, E. NO2 adsorption behaviour on LaFeO3 electrodes of YSZ-based non-nernstian electrochemical sensors. J Electroceram 26, 28–31 (2011). https://doi.org/10.1007/s10832-010-9623-6
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10832-010-9623-6