Evaluating the process of polishing borosilicate glass capillaries used for fabrication of in-vitro fertilization (iVF) micro-pipettes

Biomedical Microdevices Aims and scope Submit manuscript

Abstract

In this paper we investigate a number of gas flames for fire polishing borosilicate glass capillaries used in the manufacturing of IVF micro-pipettes. Hydrofluoric acid (HF) was also used as an alternative to finish the pipette end. Glass micro tools in the IVF industry are drawn from hollow glass capillaries of diameter 1 mm. These capillaries are cut manually to a length of 100 mm from hollow glass rods resulting in sharp and chipped edges. These capillaries are held in a customised holder having padding of soft silicone or rubber. Sharp and uneven edges of these capillaries pick up particles of rubber or soft silicone shavings, rendering them ineffective for IVF treatments. The working range of borosilicate glass is 800–1,200°C. The experiments involved analysis of fire polishing process for borosilicate glass capillaries using candle, butane, propane, 2350 butane propane, oxyacetylene gas flames, finding the optimum distance of the capillary relative to the flame, optimum time for which the capillary should be held in the flame and optimum region of the flame which gives the required temperature range. The results show that 2350 butane propane gas mix is optimum for fire polishing of borosilicate glass capillaries. The paper is concluded by comparing the results of fire polishing with the results of acid polishing, in which HF of 1.6% concentration is used to etch the ends of the borosilicate glass pipettes.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Fig. 1
Fig. 2
Fig. 3
Fig. 4
Fig. 5
Fig. 6
Fig. 7
Fig. 8
Fig. 9

Reference

  • I. Avramov, T. Vassilev, The glass transition temperature of silicate and borate glasses. J. Non-Cryst. Solids 351, 472–476 (2004)

    Article  Google Scholar 

  • V Babrauskas, Temperatures in Flames and Fires (Fire Science and Technology, Issaquah, WA, 1998)

  • M. Goodman, S Lockery, Pressure polishing: a method for re-shaping patch pipettes during fire polishing. J. Neurosci. Methods 100, 13–15 (2000)

    Article  Google Scholar 

  • M. Harz, H Engleke, Curvature Changing or flattening of anodically bonded silicone and borosilicate glass. Sens. Actuators 55, 201–209, (1996)

    Article  Google Scholar 

  • W. Kingery, H. Bowen, D. Uhlmann, Glasses, Introduction to Ceramics, 2nd edn. (John Wiley and Sons, New York, 1976), pp. 7.1–7.20

    Google Scholar 

  • R. Lehman, The Mechanical Properties of Glass, Theoretical Strength, Practical Strength, Fatigue, Flaws, Toughness, Chemical Processes, Glass Engineering 150:312, (Department of Ceramics and Material Engineering, Rutgers University New Jersey USA, 1998), pp. 1–15

    Google Scholar 

  • Schott, Types of technical glasses, physical and technical properties (Schott Technical Glasses, Germany, 2000), pp. 1–40

  • O. Sylvania, Thermal performance of borosilicate tubing. Tech. Inf. Bull. 1–8, (2004)

  • V. Venkatesh, S. Mahadevan, electro-chemical mechanical polishing of copper and chemical mechanical polishing of glass, J. Mater. Process. Technol. 149, 493–498, (2004)

    Article  Google Scholar 

  • W. Xiaosheng, C. Wenyuan, W. Lijiang, L. Xiangyang, Z. Weiping, C. Xiaomei, Non-abrasive polishing of glass, Int. J. Mach. Tools Manuf. 42, 449–456, (2002)

    Article  Google Scholar 

Download references

Author information

Authors and Affiliations

Authors

Corresponding author

Correspondence to Mayur Yaul.

Rights and permissions

Reprints and permissions

About this article

Cite this article

Yaul, M., Bhatti, R. & Lawrence, S. Evaluating the process of polishing borosilicate glass capillaries used for fabrication of in-vitro fertilization (iVF) micro-pipettes. Biomed Microdevices 10, 123–128 (2008). https://doi.org/10.1007/s10544-007-9117-8

Download citation

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s10544-007-9117-8

Keywords

Navigation