NMR Analysis to Identify Biuret Groups in Common Polyureas

  • Article
  • Published:
Chinese Journal of Polymer Science Aims and scope Submit manuscript

Abstract

Polyureas (PU) are well known as a class of high impact engineering materials, and widely used also in emerging advanced applications. As a general observation, most of them are only soluble in a very limited number of highly protonic solvents, which makes their chemical structure analysis a great challenge. Besides the presence of abundant hydrogen bonding, the poor solubility of PU in common organic solvents is often ascribed to the formation of biuret crosslinking in their molecular chains. To clarify the presence of biuret groups in PU has been of great interest. To this end, two samples, based on hexamethylene diisocyanate (HDI) and toluene diisocyanate (TDI) respectively, were synthesized by precipitation polymerization of each of these diisocyanates in water-acetone at 30 °C. Their chemical structures were analyzed by high resolution magic angle spinning (HR-MAS) NMR, and through comparison of their NMR spectra with those of specially prepared biuret-containing polyurea oligomers, it was concluded that biuret group was absent in all the PU prepared at 30 °C. In addition, this NMR analysis was also applied to a PU obtained by copolymerization of TDI with ethylene diamine (EDA) and water at 65 °C in EDA aqueous solution. It was confirmed that biuret unit was also absent in this PU and that EDA was more active than water towards TDI. The presence of EDA was crucial to the formation of uniform PU microspheres. This study provides therefore a reliable method for the analysis of PU chemical structure.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Similar content being viewed by others

References

  1. Davidson, J. S.; Fisher, J. W.; Hammons, M. I.; Porter, J. R.; Dinan, R. J. Failure mechanisms of polymer-reinforced concrete masonry walls subjected to blast. J. Struct. Eng. 2005, 131(8), 1194–1205.

    Article  Google Scholar 

  2. Mohotti, D.; Ngo, T.; Mendis, P.; Raman, S. N. Polyurea coated composite aluminium plates subjected to high velocity projectile impact. Mater. Design 2013, 52(24), 1–16.

    Article  CAS  Google Scholar 

  3. Samiee, A.; Amirkhizi, A. V.; Nemat-Naser, S. Numerical study of the effect of polyurea on the performance of steel plates under blast loads. Mech. Mater. 2013, 64(9), 1–10.

    Article  Google Scholar 

  4. Ley, S. V.; Mitchell, C.; Pears, D.; Ramarao, C.; Yu, J. Q.; Zhou, W. Recyclable polyurea microencapsulated Pd nanoparticles: An efficient catalyst for hydrogenolysis of epoxides. Org. Lett. 2003, 5(24), 4665–4668.

    Article  CAS  PubMed  Google Scholar 

  5. Han, H.; Zhou, Y.; Li, S.; Wang, Y.; Kong, X. Z. Immobilization of lipase from pseudomon as fluorescens on porous polyurea and its application in kinetic resolution of racemic 1-phenylethanol. ACS Appl. Mater. Interfaces 2016, 8(39), 25714–25724.

    Article  CAS  PubMed  Google Scholar 

  6. Jiang, X.; Yu, Y.; Li, X.; Kong, X. Z. High yield preparation of uniform polyurea microspheres through precipitation polymerization and their application as laccase immobilization support. Chem. Eng. J. 2017, 328, 1043–1050.

    Article  CAS  Google Scholar 

  7. Jacquemond, M.; Jeckelmann, N.; Ouali, L.; Haefliger, O. P. Perfume-containing polyurea microcapsules with undetectable levels of free isocyanates. J. Appl. Polym. Sci. 2009, 114(5), 3074–3080.

    Article  CAS  Google Scholar 

  8. Li, J.; Hughes, A. D.; Kalantar, T. H.; Drake, I. J.; Tucker, C. J.; Moore, J. S. Pickering-emulsion-templated encapsulation of a hydrophilic amine and its enhanced stability using poly(allyl amine). ACS Macro Lett. 2014, 3(10), 976–980.

    Article  CAS  Google Scholar 

  9. Chen, L.; Xu, L.; Shang, H.; Zhang. Z. Microencapsulation of butyl stearate as a phase change material by interfacial polycondensation in a polyurea system. Energ. Convers. Manage. 2009, 50(3), 723–729.

    Article  CAS  Google Scholar 

  10. Ying, H.; Zhang, Y.; Cheng, J. Dynamic urea bond for the design of reversible and self-healing polymers. Nat. Commun. 2014, 5, 3218.

    Article  CAS  PubMed  PubMed Central  Google Scholar 

  11. Howarth, G. Polyurethanes, polyurethane dispersions and polyureas: Past, present and future. Surf. Coat. Int. Part B Coat. Trans. 2003, 86(2), 111–118.

    Article  CAS  Google Scholar 

  12. Jiang, X.; Li, X.; Zhu, X.; Kong, X. Z. Preparation of highly uniform polyurea microspheres through precipitation polymerization and their characterization. Ind. Eng. Chem. Res. 2016, 55(44), 11528–11535.

    Article  CAS  Google Scholar 

  13. Jiang, X.; Kong, X. Z.; Zhu, X. A Novel protocol for the preparation of uniform polymer microspheres with high yields through step polymerization of isophorone diisocyanate. J. Polym. Sci., Part A: Polym. Chem. 2011, 49(20), 4492–4497.

    Article  CAS  Google Scholar 

  14. Sumi, M.; Chokki, Y.; Nakai, Y.; Nakabayashi, M.; Kanzawa, T. Studies on the structure of polyurethane elastomers. I. NMR spectra of the model compounds and some linear polyurethanes. Die Makromol. Chem. 1964, 78(1), 146–156.

    CAS  Google Scholar 

  15. Chattopadhyay, D. K.; Raju, K. V. S. N. Structural engineering of polyurethane coatings for high performance applications. Prog. Polym. Sci. 2007, 32(3), 352–418.

    Article  CAS  Google Scholar 

  16. Suzuoki, K.; Kagawa, K.; Fukuma, K.; Uda, B.; Ohmura, J. The analysis of synthetic and side reactions of polyurethaneurea. Nippon Gomu Kyokaishi 1999, 72, 139–143.

    Article  CAS  Google Scholar 

  17. Mathisen, R. J.; Yoo, J. K.; Sung, C. S. P. Dye labeling technique for monitoring the cure of polyimides and polyureas: Model compound studies. Macromolecules 1987, 20(6), 1414–1416.

    Article  CAS  Google Scholar 

  18. Okuto, H. Studies on the structure of polyurethane elastomers. II. High resolution NMR spectroscopic determination of allophanate and biuret linkages in the cured polyurethane elastomer: Degradation by amine. Die Makromol. Chem. 1966, 98(1), 148–163.

    CAS  Google Scholar 

  19. Delebecq, E.; Pascault, J.; Boutevin, B.; Ganachaud, F. On the Versatility of urethane/urea bonds: Reversibility, blocked isocyanate, and non-isocyanate polyurethane. Chem. Rev. 2013, 113(1), 80–118.

    Article  CAS  PubMed  Google Scholar 

  20. Zhang, X.; Zhang, X. Y.; He, Y.; Chen, H. Progress in synthesis and characterization of HDI biuret. Pain Coat. Ind. 2011, 41(10), 71–75.

    CAS  Google Scholar 

  21. Lapprand, A.; Boisson, F.; Delolme, F.; Méchin, F.; Pascault, J. P. Reactivity of isocyanates with urethanes: conditions for allophanate formation. Polym. Degrad. Stab. 2005, 90(2), 363–373.

    Article  CAS  Google Scholar 

  22. Jiang, X.; Zhu, X.; Arnold, A. A.; Kong, X. Z.; Claverie, J. P. Polyurea structure characterization by HR-MAS NMR spectroscopy. Ind. Eng. Chem. Res. 2017, 56(11), 2993–2998.

    Article  CAS  Google Scholar 

  23. Han, H.; Li, S.; Zhu, X.; Jiang, X.; Kong, X. Z. One step preparation of porous polyurea by reaction of toluene diisocyanate with water and its characterization. RSC Adv. 2014, 4(63), 33520–33529.

    Article  CAS  Google Scholar 

  24. Jiang, X.; Zhu, X.; Kong, X. Z. A facile route to preparation of uniform polymer microspheres by quiescent polymerization with reactor standing still without any stirring. Chem. Eng. J. 2012, 213(12), 214–217.

    Article  CAS  Google Scholar 

  25. Kong, X. Z.; Jiang, W.; Jiang, X.; Zhu, X. Preparation of coreshell and hollow polyurea microspheres via precipitation polymerization using polyamine as crosslinker monomer. Polym. Chem. 2013, 4(24), 5776–5784.

    Article  CAS  Google Scholar 

  26. Li, S. S.; Han, H.; Zhu, X.; Jiang, X.; Kong, X. Z. Preparation and formation mechanism of porous polyurea by reaction of toluene diisocyanate with water and its Application as adsorbent for anionic dye removal. Chinese J. Polym. Sci. 2015, 33(8), 1196–1210.

    Article  CAS  Google Scholar 

  27. Li, S.; Zhu, X.; Kong, X. Z.; Jiang, X. One step synthesis of porous polyurea by using TDI and EDA and its characterization. Acta Polymerica Sinica (in Chinese) 2016, (3), 391–398.

    Google Scholar 

  28. Yang, Y.; Jiang, X.; Zhu, X.; Kong, X. Z. A facile pathway to polyurea nanofiber fabrication and polymer morphology control in copolymerization of oxydianiline and toluene diisocyanate in acetone. RSC Adv. 2015, 5(10), 7426–7432.

    Article  CAS  Google Scholar 

  29. Alam, T. M.; Jenkins, J. E. “Advanced Aspects of Spectroscopy”, Intech, Croatia, 2012, p. 279–301.

    Google Scholar 

  30. Li, S.; Zhao, J.; Zhang, Z.; Zhang, J.; Yang, W. Aliphatic thermoplastic polyurethane-ureas and polyureas synthesized through a non-isocyanate route. RSC Adv. 2015, 5(9), 6843–6852.

    Article  CAS  Google Scholar 

  31. Harris, R. F.; Kinney, J. E.; Savina, M. R.; Jeor, V. L. S.; Bicerano, J.; Durvasula, V. R.; Moreno, L. N. Synthesis and characterization of urea-based polyureas: 1. Urea-terminated poly(1,6-hexamethyleneurea) polyol dispersions. Polymer 1995, 36(22), 4275–4285.

    CAS  Google Scholar 

  32. Edwards, P. A.; Striemer, G.; Webster, D. C. Synthesis, characterization and self-crosslinking of glycidyl carbamate functional resins. Prog. Org. Coat. 2006, 57(2), 128–139.

    Article  CAS  Google Scholar 

  33. Wendisch, D.; Reiff, H.; Dieterich, D. Kernresonanzspektroskopische beiträge zur struktur und stereochemie von (cyclo)aliphatischen isocyanaten und deren folgeprodukten. Angew. Makromol. Chem. 1986, 141(1), 173–183.

    Article  CAS  Google Scholar 

  34. Zhang, F.; Jiang, X.; Zhu, X.; Chen, Z.; Kong, X. Z. Preparation of uniform and porous polyurea microspheres of large size through interfacial polymerization of toluene diisocyanate in water solution of ethylene diamine. Chem. Eng. J. 2016, 303, 48–55.

    Article  CAS  Google Scholar 

  35. Entelis, S. G.; Nesterov, O. V. Kinetics and mechanism of the reactions of isocyanates with compounds containing “active” hydrogen. Russ. Chem. Rev. 1966, 35(12), 917–930.

    Article  Google Scholar 

  36. Lu, X.; Wang, Y.; Wu, X. Molecular interactions in polyurea by 1-D and 2-D NMR. Polymer 1993, 34(1), 56–60.

    Article  CAS  Google Scholar 

Download references

Acknowledgments

This work was financially supported by the National Natural Science Foundation of China (Nos. 21274054, 21304038 and 51473066), Research Foundation of University of Jinan (No. XKY1604) and by Science & Technology Development Plan of Shandong Province (No. 2017GGX202009), China.

Author information

Authors and Affiliations

  1. College of Chemistry and Chemical Engineering, University of Jinan, Jinan, 250022, China

    Wei-Guang Qiu, Fei-Long Zhang, Xu-Bao Jiang & Xiang-Zheng Kong

Authors
  1. Wei-Guang Qiu
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. Fei-Long Zhang
    View author publications

    You can also search for this author in PubMed Google Scholar

  3. Xu-Bao Jiang
    View author publications

    You can also search for this author in PubMed Google Scholar

  4. Xiang-Zheng Kong
    View author publications

    You can also search for this author in PubMed Google Scholar

Corresponding authors

Correspondence to Xu-Bao Jiang or Xiang-Zheng Kong.

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Qiu, WG., Zhang, FL., Jiang, XB. et al. NMR Analysis to Identify Biuret Groups in Common Polyureas. Chin J Polym Sci 36, 1150–1156 (2018). https://doi.org/10.1007/s10118-018-2130-y

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s10118-018-2130-y

Keywords

Search

Navigation