Abstract
Photosensitive glasses are well known as materials which are micro structurable with a high aspect ratio of 20:1. Typical applications are micro mechanical, fluidic and optical components due to the very good chemical, thermal and mechanical stability of this material. Currently the aim of the work is the development of micro structured clichés made from photosensitive glass for the gravure printing of electrically functionalised inks on flexible substrates. Glass clichés with a geometrical variation of recessed cells were fabricated and tested regarding the chemical and mechanical stability using process comparable conditions. Printing tests using particle less and particle loaded electrically functionalised inks were carried out to investigate the influence of cell geometry on printed ink layers. It was found that precise dot structures will be printable if cell openings are <80 μm and cell depths are <30 μm. Resulting from this ITO was printed on flexible glass substrates with a thickness of 30 μm for high temperature treatments.
Similar content being viewed by others
References
Bock K (2005) Polymer electronics systems—polytronics. Proc IEEE 93(8)
Hübler A, Beier W, Brandt N, Fischer Th, Fügmann U, Hahn U, Zielke D (2003) Gedruckte Polymerelektronik für Verpackungen: Status Quo und Ausblick. VVD 2003 Fachtagung Verarbeitungsmaschinen und Verpackungstechnik
Japanese Patent Office (1990) Publication number 02135348 A, 24.5
Japanese Patent Office (1991) Publication number 0306939 A, 25.3
Lehmann U (1999) Druckverfahren und Einrichtung zu dessen Durchführung. Patentschrift DE 197 46 274 C 1
Ollech B (1993) Tiefdrucktechnik - Grundlagen und Verfahrensschritte der modernen Tiefdrucktechnik. Polygraph-Verlag, Frankfurt am Main
Vogel W (1992) Glaschemie. Springer, Heidelberg
Acknowledgments
This work was part of the CONTACT project (contract no.: 511562), partly financially supported by the European Commission (FP6). The authors thank the partner of the project for providing printing equipment in form of inks, plastic films and printing machines. ITO printing tests were carried out at INM Saarbrücken supported by Dr. J. Pütz.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Brokmann, U., Sönnichsen, K. & Hülsenberg, D. Application of micro structured photosensitive glass for the gravure printing process. Microsyst Technol 14, 1635–1639 (2008). https://doi.org/10.1007/s00542-008-0602-7
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s00542-008-0602-7