Abstract
Powders of (Pb0.8Ca0.2)(Ti0.99Mn0.01)O3 have been prepared by sol-gel processing. A tetragonal phase is formed after heat treatment at as low as 800°C. The tetragonality was found to be 1.053±0.005 and Curie temperature 315°C. Composite films with 0–3 connectivity were prepared from 800°C heat treated powders and P(VDF-TrFE) by the solvent casting technique. Composites poled at 20 MV/m, exhibited a pyroelectric coefficient of 17.4 μC/m2K and a pyroelectric figure of merit (FOMp=p/ε) of 0.51 μC/m2K.
Similar content being viewed by others
References
A.J. Moulson and J.M. Herbert,Electroceramics (Chapman and Hall, 1990).
S.L. Swartz, IEEE Trans. on Electrical Insulation22(5) (1990).
B. Jimenez et al., Ferroelectrics87, 97 (1988).
Y. Yamashita, Jap. Journal of Applied Physics22(2), 40 (1983).
J.B. Blum and S.R. Gurkovich, Journal of Materials Science20, 4479 (1985).
R. Sierra and M.L. Calzada, Mat. Res. Bull.30(1), (1995).
M. Maeda, H. Ishida, K. Ko Ko, and I. Susuki, Jpn. J. Appl. Phys.32, 4136 (1993).
C.J. Dias and D.K. Das-Gupta, J. Appl. Phys.74(10), 15 (1993).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Igreja, R., Dias, C.J. & Marat-Mendes, J.N. Processing and characterization of sol-gel derived modified PbTiO3 for ferroelectric composite applications. J Sol-Gel Sci Technol 8, 721–723 (1997). https://doi.org/10.1007/BF02436929
Issue Date:
DOI: https://doi.org/10.1007/BF02436929