Abstract
The phosphor cation retards BaTiO3 formation during the first reaction stage, and favours Ba2TiO4 formation. As a consequence, the end of the reaction is only accomplished at 1150 °C. The average particle size of the synthesized powder, after attrition milling was <1.0 μm. Isopressed bars were sintered from 1200–1400 °C. Dilatometric measurements showed the existence of two sintering mechanisms; these were confirmed by means of isothermal sintering experiments. Microstructural development at low sintering temperature differs from that corresponding to higher ones. Very high permittivity values were measured in the 1325–1350 °C sintered samples. This anomalous dielectric behaviour is associated with the presence of phosphor.
Similar content being viewed by others
References
I. Burn, M. T. Raad andK. Sasaki, in “Ceramic transactions”, Vol. 8, edited by H. C. Ling and M. F. Yan (American Ceramic Society Inc., Westerville, OH, 1990) pp. 20–34.
Y. Sakabe, T. Takagi, K. Wakino andD. M. Smyth, “Advances in ceramics”, Vol. 19, edited by J. B. Blum and W. R. Cannon (American Ceramic Society Inc., Westerville, OH, 1986) pp. 103–15
K. R. Mikeska andW. R. Cannon Coll. Surf. 29 (1988) 305.
W. R. Cannon, J. R. Morris andK. R. Mikeska, in “Advances in ceramics”, Vol. 19, edited by J. B. Blum, and W. R. Cannon (American Ceramic Society Inc., Westerville, OH, 1986) pp. 161–74
H. M. O'Bryan Jr,Am. Ceram. Soc. Bull. 66 (1987) 677.
J. F. Fernández, P. Durán andC. Moure,J. Mater. Sci. 26 (1991) 3257.
A. C. Caballero, PhD thesis, Universidad Autónoma de Madrid, Madrid (1994).
R. A. McCauley andF. A. Hummel,Trans. Brit. Ceram. Soc. 67 (1968) 619.
J. S. Choi andH. G. Kim,J. Mater. Sci. 27 (1992) 1285.
A. Beauger, J. C. Mutin andJ. C. Niepce,J. Mater. Sci. 18 (1983) 2543.
A. K. Maurice andR. C. Buchanan,Ferroelectrics,74 (1987) 61.
J. F. Fernández, P. Durán andC. Moure,ibid.,106 (1990) 381.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Caballero, A.C., Fernández, J.F., Durán, P. et al. Phosphor-doped BaTiO3: Microstructure development and dielectric properties. J Mater Sci 30, 3799–3804 (1995). https://doi.org/10.1007/BF01153937
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/BF01153937