Abstract
Three different types of SiC preforms, with open porosities between 60 and 70%, were prepared by pyrolysis of polysilanes and polycarbosilanes at 1670 K. some samples of each type of SiC structure were oxidized in air at 1070 K to promote wetting by the glass melt. Preforms were then applied for gas pressure infiltration with an alumosilicate glass melt at 1670 K in 3 MPa argon, and the influence of pore-size distribution and surface composition on infiltration time was investigated. The composition of the precursors was determined by chemical analysis, and pyrolysed SiC was analysed by thermal decomposition. The porosity and pore-size distribution of the SiC-preforms were measured on photographs of sample cross-sections. The SiC-glass composites were examined by light microscopy, scanning electron microscopy and electron scanning microanalysis.
Similar content being viewed by others
References
S. Yajima,Bull. Amer. Ceram. Soc. 62 (1983) 893.
D. Mocaer andR. Pailler,J. European Ceram. Soc. 12 (1993) 27.
H.-P. Martin, PhD thesis, Freiberg (1994).
N. R. Langley, G. E. Legrow andJ. Lipowitz, in “Fiber reinforced ceramic composites (Materials Processing and Technology)”, edited by K. S. Mazdiyasni (Noyes Publications, Park Ridge, NJ, 1990) p. 63.
Z.-F. Zhang, F. Babonneau, R. M. Laine, Y. Mu, J. F. Harrad andJ. A. Rahn,J. Amer. Ceram. Soc. 74 (1991) 670.
K. S. Mazdiyasni, R. West, L. D. David,ibid. 61 (1978) 504.
Y. Katsura, N. Sato, H. Shikano andH. Ikami, in Proceedings of the 12th and 13th International Colloquium on Refractories, Aachen October 1989, p. 27.
K. Langguth,Ceram. Int. 21 (1995) 237.
K. Wernowsky, Master thesis, Freiberg (1991).
R. Richter, G. Roewer, K. Leo andB. Thomas,Freiberger Forschungshefte A 832 (1993) 99.
H.-P. Martin, E. Müller, R. Richter, G. Roewer andE. Brendler,J. Mater. Sci. in press.
W. Habel, B. Harnack, C. Nover andP. Sartori,J. Organomettalic Chem. 467 (1994) 13.
S. Böckle, Master thesis, Freiberg (1993).
F. Delanney,J. Mater. Sci. 22 (1987) 1.
J. J. Brennan andS. R. Nutt,J. Amer. Ceram. Soc. 75 (1992) 1205.
A. Jha andM. D. Moore,Glass Technol. 33 (1992) 30.
J. Y. Hsu andR. F. Speyer,J. Mater. Sci. 27 (1992) 374.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Langguth, K., Böckle, S., Müller, E. et al. Polysilane-derived porous SiC preforms for the preparation of SiC-glass composites. J Mater Sci 30, 5973–5978 (1995). https://doi.org/10.1007/BF01151514
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/BF01151514