Abstract
In the system Li2O-Al2O3-SiO2, Li4SiO4 forms two limited ranges of solid solutions: Li4+x Si1−x Al x O4: 0 < x ≲ 0.4, containing interstitial Li+ ions and Li4−3y Al y SiO4: 0⩽y≲ 0.06, containing Li+ vacancies. The a.c. conductivity of polycrystalline samples of several compositions was measured over a range of frequency (2×102 to 5×104 Hz) and temperature (25 to 500°C). Both solid solutions, especially the Li+ interstitial ones, have markedly higher conductivity than has stoichiometric Li4SiO4. This is due to an increase in the number of mobile ions and a decrease in the activation energy for conduction in the solid solutions.
Similar content being viewed by others
References
A. R. West, J. Appl. Electrochem. 3 (1973) 727.
I. M. Hodge, M. D. Ingram and A. R. West, J. Amer. Ceram. Soc. 59 (1975) 360.
Y. -Wu. Hu, I. D. Raistrick and R. A. Huggins, J. Electrochem. Soc. 124 (1977) 1240.
R. D. Shannon, B. E. Taylor, A. D. English and T. Berzins, Electrochim. Acta 22 (1977) 783.
R. A. Huggins, ibid. 22 (1977) 773.
A. Khorassani, G. Izquierdo and A. R. West, Mater. Res. Bull. 16 (1981) 1561.
A. Khorassani and A. R. West, Solid State Ionics 7 (1982) 1.
Idem, J. Solid State Chem. in press.
A. R. West and F. P. Glasser, J. Mater. Sci. 5 (1970) 557.
D. Tranqui, R. D. Shannon, H. Y. Chen, S. Ijima and W. H. Baur, Acta Cryst. B35 (1979) 2479.
H. Völlenkle, A. Wittmann and H. Now-Otny, Monat, Chemie 99 (1968) 1360.
A. R. West and P. G. Bruce, Acta Cryst. B38 (1982) 1891.
W. H. Baur, Mater. Res. Bull. 16 (1981) 339.
T. Asai and S. Kawai, Solid State Commun. 36 (1980) 891.
W. H. Baur and T. Ohta, J. Solid State Chem. 44 (1982) 50.
B. Di Pietro and B. Scrosati, J. Power Sources 2 (1977) 387.
A. K. Jonscher, Nature 267 (1977) 673.
D. P. Almond, G. K. Duncan and A. R. West, Solid State Ionics in press.
J. C. Wang, M. Gaffari and S. Choi, J. Chem. Phys. 63 (1975) 772.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Jackowska, K., West, A.R. Ionic conductivity of Li4SiO4 solid solutions in the system Li2O-Al2O3-SiO2 . J Mater Sci 18, 2380–2384 (1983). https://doi.org/10.1007/BF00541842
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/BF00541842