Abstract
A systematic study has been carried out in Fe-Ni as well as Fe-Ni-Cr alloys to understand whether the factors related to the burst temperature or alloy composition are responsible for various morphologies as well as mean plate dimensions. A systematic procedure has been adopted to give a set of Fe-Ni-Cr alloys with constant transformation burst temperature (M b ). While maintaining theM b constant, it is found that Cr replaces more and more Ni with further additions. The martensitic transformation progresses predominantly through a spreading-out process. The aspect ratio (c/r) follows a parabolic relation withM b , whereas it is linear with respect to Ni content in the case of Fe-Ni alloys. In Fe-Ni-Cr alloys, the aspect ratio, however, does not show any relationship with composition at 133 K. The appearance of different morphologies and the variation in different features within a morphology are seen in alloys with different compositions having the sameM b .
Similar content being viewed by others
References
R.G. Davies and C.L. Magee:Metall. Trans., 1971, vol. 2, pp. 1939- 47.
Gareth Thomas:Metall. Trans., 1971, vol. 2, pp. 2373–85.
G. Krauss and A.R. Marder:Metall. Trans., 1971, vol. 2, pp. 2343–57.
T. Maki, S. Shimooka, M. Umemoto, and I. Tamura:Trans. JIM, 1972, vol. 13, p. 400.
M. Umemoto, E. Yoshitake, and I. Tamura:J. Mater. Sci., 1983, vol. 18, p. 2893.
M. Laverroux and A. Pineau:Scripta Metall., 1974, vol. 8, p. 351.
S.R. Pati and M. Cohen:Acta Metall., 1969, vol. 17, p. 189.
D.G. Mcmurtrie and C.L. Magee:Metall. Trans., 1970, vol. 1, pp. 3185–91.
W.Y.C. Chen and P.G. Winchell:Metall Trans. A, 1976, vol. 7A, pp. 1177–82.
W.Y.C. Chen, E.N. Jones, and P.G. Winchell:Metall. Trans. A, 1978, vol. 9A, pp. 1659–61.
J.R.C. Guimaraes and J.C. Gomes:Acta Metall., 1978, vol. 26, p. 1591.
J.R.C. Guimaraes and J.C. Gomes:Metall Trans. A, 1979, vol. 10A, pp. 109–12.
T.N. Durlu and J.W. Christian:Proc. Int. Conf. on Martensitic Transformations, Cambridge, MA, 1979, p. 343.
J.R.C. Guimaraes and J.C. Gomes:Proc. Int. Conf. on Martensitic Transformations, Cambridge, MA, 1979, pp. 59.
R. Datta: Ph.D. Thesis, Indian Institute of Technology, Delhi, India, 1982.
G. Ghosh: Ph.D. Thesis, Indian Institute of Technology, Delhi, India, 1986.
R. Datta and V. Raghavan:Mater Sci. Eng., 1982, vol. 55, p. 239.
R. Datta and V. Raghavan:J. Phys., 1982, vol C4, p. 541.
G. Ghosh and V. Raghavan:Mater. Sci. Eng., 1986, vol. 79, p. 223.
R.L. Fullman:Trans. AIME, 1953, vol. 197, p. 447.
C.S. Smith and L. Guttman:Trans. AIME, 1953, vol. 197, p. 81.
M. Umemoto and W.S. Owen:Metall. Trans., 1974, vol. 5, pp. 2041–46.
R.G.B. Yeo:Trans. AIME, 1963, vol. 227, p. 887.
K. Ishida and Nishizawa:Trans. JIM, 1974, vol. 15, p. 217.
J.F. Breedis:Trans. Am. Inst. Min. Metall. Eng., 1964, vol. 230, p. 1583.
Y. Imai and M. Izumiyama:Sci. Rep. Tohoku Univ., 1965, Ser. 4, vol. 17, p. 135.
W.K.C. Jones and A.R. Entwisle:Met. Sci. J., 1971, vol. 5, p. 190.
L. Kaufman and M. Cohen:Met. Sci. J., 1956, vol. 206, p. 1393.
J. Philibert: Thesis, University of Paris, Paris, 1956, no. 139(A).
H. Flor, H.J. Gudladt, and Ch. Schwink:Acta Metall., 1980, vol. 28, p. 1611.
A.R. Entwisle and J.A. Feeney:Inst. Met., Monogr. Rep. Ser, 1968, vol. 33, p. 156.
T. Maki, S. Shimooka, S. Fujiwara, and I. Tamura:Trans. Jpn. Inst. Met, 1975, vol. 16, p. 35.
M. Watanabe and CM. Wayman:Metall. Trans., 1971, vol. 2, pp. 2221–27.
M. Umemoto and C.M. Wayman:Acta Metall., 1978, vol. 26, p. 1529.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Visvesvaran, P. A study on morphology and plate mean dimensions in Fe-Ni and Fe-Ni-Cr alloys. Metall Mater Trans A 27, 973–980 (1996). https://doi.org/10.1007/BF02649765
Received:
Issue Date:
DOI: https://doi.org/10.1007/BF02649765