Abstract
The quantitative dependence of Young's modulus and fracture behaviour on the angle between the tensile axis and the orientation direction has been determined for oriented polyethylene with lamellae of chain-extended dimensions. The form of the modulus dependence was similar to that for the majority of oriented polymers which have been studied, but the fracture behaviour was atypical, ductility only being obtained when the test axis was parallel to the orientation direction, with brittle fracture occurring in all other directions for all except very high molecular mass materials.
The behaviour of this material in compression alongc has also been studied; in this case kink bands andc-axis cleavage were observed. It is shown that kink band formation may be explained solely by uniformc axis shear deformation of the lamellar crystals.
Similar content being viewed by others
References
D. C. Bassett,Polymer 17 (1976) 460.
Idem, High. Temp. High. Press. 9 (1977) 553.
D. C. Bassett andD. R. Carder,Phil. Mag. 28 (1973) 513.
D. C. Bassett, S. Block andG. J. Piermarini,J. Appl. Phys. 45 (1974) 4146.
D. C. Bassett andD. R. Carder,Phil. Mag. 28 (1973) 535.
D. C. Bassett, B. A. Khalifa andR. H. Olley,Polymer 17 (1976) 284.
Idem, J. Polymer Sci. Polymer Phys. Ed. 15 (1977) 995.
R. H. Olley andD. C. Bassett,ibid. 15 (1977) 1011.
J. F. Nye, “Physical Properties of Crystals” (Oxford, 1957) Ch. 8.
R. G. C. Arridge andM. J. Folkes,Polymer 17 (1976) 495.
K. Thomas andD. E. Meyer,Plast. & Rubber Mater. & Appl. 1 (1976) 136.
R. G. Robertson,J. Polymer Sci. A-2 7 (1969) 1315.
R. W. K. Honeycombe, “The Plastic Deformation of Metals” (Arnold, London, 1968) Ch. 8.
D. W. Hadley, P. R. Pinnock andI. M. Ward,J. Mater. Sci. 4 (1969) 152.
R. Davitt, Ph.D. Thesis, University of Reading (1973).
G. Capaccio andI. M. Ward,Polymer 15 (1974) 233.
A. Keller andJ. G. Rider,J. Mater. Sci. 1 (1966) 389.
D. C. Bassett andA. M. Hodge, (to be published).
Idem, Proc. Roy. Soc. A 359 (1978) 121.
G. E. Attenburrow andD. C. Bassett,J. Mater. Sci. 12 (1977) 192.
K. Shigematsu, K. Imada andM. Takayanagi,J. Polymer Sci. Polymer Phys. Ed. 13 (1975) 73.
A. G. Kilbeck andD. R. Uhlmann,J. Polymer Sci. Polymer Phys. Ed. 14 (1976) 1257.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Attenburrow, G.E., Bassett, D.C. Compliances and failure modes of oriented chain-extended polyethylene. J Mater Sci 14, 2679–2687 (1979). https://doi.org/10.1007/BF00610639
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/BF00610639