Abstract
Formation of boehmite sols from aluminium alkoxides was studied by X-ray diffraction, IR-spectroscopy, DLS (Dynamic Light Scattering) and other methods. It was found that the distortion of the boehmite crystal lattice occurs under the electrolyte sol formation processes. The surface charges were evaluated to explain the observed changes in X-ray patterns and IR-spectra of the boehmite samples and the causes that bring about these changes. The influence of the peptizing process on γ-Al2O3 specific surface was also studied.
Similar content being viewed by others
References
F.W. Dynys and H.W. Holloran, in Ultrastructure Processing of Ceramics, Glasses and Composites, edited by L.L. Hench and D.R. Ulrich (N.Y., 1984), p. 142.
M.A. Leitheiser and H.G. Sowman, Non-Fused Aluminium Oxides-Based Abrasive Minerals, U.S. Patent No. 4314827, 1982.
M.G. Schwabel, Process for Durable Sol-Gel Produced Alumina-Based Ceramics, Abrasive Grain and Abrasive Products, U.S. Patent No. 4744802, 1988.
Y. Suwa, R. Roy, and S. Komarneni, J. Amer. Ceram. Soc. 68(9), 238 (1985).
B.E. Yoldas, J. Appl. Chem. Biotech. 23(1), 803, (1973).
P.R. Reichertz and W.J. Yost, J. Chem. Phys. 14(8), 495 (1946).
B.E. Yoldas, Amer. Ceram. Soc. Bull. 54(3), 289 (1975).
G.W. Scherer, J. Non-Cryst. Solids 121(1–3), 104 (1900).
A.R. Cooper, in Ceramics Processing Before Firing, edited by G.J. Ohola and L.L. Hench (N.Y., 1978).
J. Zarzycki, M. Prassas, and J. Phalippou, J. Mater. Sci. 17, 3371 (1982).
P.N. Pusey, Diffusion of Identification and Non-Interacting of the Macromolecula, in Photon Correlation and Light Beating Spectroscopy, edited by H.Z. Comminns and E.R. Pike (N.Y. and London, 1974).
R.I. Zakharchenya, I.K. Meshkovskii, and F.S. Kaplan, DAN (Dokl. Akad Nauk, 1990), 314(2), p. 393 (Russia).
R. Sprycha, J. Colloid. Interface Sci. 127(1) 1 (1989).
Rights and permissions
About this article
Cite this article
Zakharchenya, R.I. Influence of peptization on the properties of alumina produced from boehmite sols. J Sol-Gel Sci Technol 6, 179–186 (1996). https://doi.org/10.1007/BF00425975
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/BF00425975