Abstract
Using 4-aminopyridine as the structure-directing agent(SDA), a new open-framework zinc phosphite, (C5H7N2)2·[Zn3(HPO3)4](ZnHPO-CJ70), was synthesized under hydrothermal condition. Single-crystal X-ray diffraction analysis reveals that ZnHPO-CJ70 is constructed by the strictly alternating ZnO4 tetrahedra and HPO3 pseudo-pyramids, with their vertexes linked to generate a three-dimensional(3D) open framework with intersecting 8- and 12-ring channels. Further characterizations of ZnHPO-CJ70 were performed by means of X-ray powder diffraction(XRD), elemental analysis(ICP, CHN), infrared spectroscopy(IR) and thermogravimetric(TG) analyses. The results of luminescent test shows that ZnHPO-CJ70 exhibits strong fluorescence emissions in the solid state at room temperature.
Similar content being viewed by others
References
Li Y., Yu J. H., Chem. Rev., 2014, 114(14), 7268
Li Y., Yu J. H., Xu R. R., Baerlocher C., McCusker L. B., Angew. Chem. Int. Ed., 2008, 47, 4401
Li Y., Yu J. H., Xu R. R., Angew. Chem. Int. Ed., 2013, 52, 1673
Mallouk T. E., Gavin J. A., Acc. Chem. Res., 1998, 31(5), 209
Seo J. S., Whang D., Lee H., Jeon Y. J., Kim K., Nature, 2000, 404, 982
Cao G., Garcia M. E., Alcalá M., Burgess L. F., Mallouk T. E., J. Am. Chem. Soc., 1992, 114(19), 7574
Joy A., Uppili S., Netherton M. R., Scheffer J. R., Ramamurthy V., J. Am. Chem. Soc., 2000, 122(4), 728
Yu J. H., Xu R. R., Chem. Soc. Rev., 2006, 35, 593
Yu J. H., Xu R. R., Acc. Chem. Res., 2010, 43(9), 1195
Wang Z. P., Yu J. H., Xu R. R., Chem. Soc. Rev., 2012, 41, 1729
Song X. W., Li Y., Gan L., Wang Z. P., Yu J. H., Xu R. R., Angew. Chem. Int. Ed., 2009, 48, 314
Chiang R. K., Chuang N. T., J. Solid State Chem., 2005, 178(10), 3040
Luo X. C., Luo D. B., Gong M. C., Chen Y. Q., Lin Z. E., Cryst. Eng. Comm., 2011, 13(11), 3646
Zhao L., Li J. Y., Chen P., Li G. H., Yu J. H., Xu R. R., Chem. Mater., 2008, 20(1), 17
Xing H. Z., Yang W. T., Su T., Li Y., Xu J., Nakano T., Yu J. H., Xu R. R., Angew. Chem. Int. Ed., 2010, 49(13), 2328
Luo X. C., Luo D. B., Zeng H. M., Gong M. C., Chen Y. Q., Lin Z. E., Inorg. Chem., 2011, 50(18), 8697
Lin H. Y., Chin C. Y., Huang H. L., Huang W. Y., Sie M. J., Huang L. H., Lee Y. H., Lin C. H., Lii K. H., Bu X. H., Wang S. L., Science, 2013, 339, 811
Harrison W. T. A., J. Solid State Chem., 2001, 160(1), 4
Harrison W. T. A., Phillips M. L. F., Nenoff T. M., Int. J. Inorg. Mater., 2001, 3(7), 1033
Lin Z. E., Zhang J., Zheng S. T., Yang G. Y., J. Mater. Chem., 2004, 14, 1652
Chen W. B., Li N., Xiang S. H., J. Solid State Chem., 2004, 177(9), 3229
Wang X. L., Yan Y., Wu J. B., Zou Y. C., Zhang C. Q., Li J. Y., Chem. J. Chinese Universities, 2014, 35(6), 1142
Fernández S., Mesa J. L., Lezama L., Arriortua M. I., Rojo T., Chem. Mater., 2002, 14(5), 2300
Fernández S., Mesa J. L., Pizarro J. L., Lezama L., Arriortua M. I., Rojo T., Chem. Mater., 2003, 15(5), 1204
Zhang D., Yue H. J., Shi Z., Guo M., Feng S. H., Micropor. Mesopor. Mater., 2005, 82(1/2), 209
Fan J., Yee G. T., Wang G. B., Hanson B. E., Inorg. Chem., 2006, 45(2), 599
Li G. J., Xing Y., Song S. Y., J. Solid State Chem., 2008, 181(4), 943
Liu X. C., Xing Y., Liu X. Z., Cryst. Eng. Comm, 2010, 12, 383
Liu X. C., Xing Y., Wang X. L., Xu H. B., Liu X. Z., Shao K. Z., Su Z. M., Chem. Commun., 2010, 46, 2614
Mandal S., Pati S. K., Green M. A., Natarajan S., Chem. Mater., 2005, 17(3), 638
Fan Y., Song T. Y., Li G. H., Shi Z., Yu G. H., Xu J. N., Feng S. H., Inorg. Chem. Commun., 2005, 8(8), 661
Fernández S., Mesa J. L., Pizarro J. L., Lezama L., Arriortua M. I., Olazcuaga R., Rojo T., Chem. Mater., 2000, 12(8), 2092
Fernández S., Pizarro J. L., Mesa J. L., Lezama L., Olazcuaga R., Rojo T., Inorg. Chem., 2001, 40(14), 3476
Li N., Xiang S. H., J. Mater. Chem., 2002, 12, 1397
Li N., Ma Y. F., Xiang S. H., Guan N. J., Chem. Mater., 2006, 18(4), 975
Lu A. L., Song H. B., Li N., Xiang S. H., Guan N. J., Wang H. G., Chem. Mater., 2007, 19(17), 4142
Xiang Y., Zhang L.W., Chen W. H., Chen J. Z., Zeng Q. X., Z. Anorg. Allg. Chem., 2007, 633(10), 1727
Harrison W. T. A., Phillips M. L. F., Stanchfield J., Nenoff T. M., Inorg. Chem., 2001, 40(5), 895
Liang J., Li J. Y., Yu J. H., Chen P., Fang Q. R., Sun F. X., Xu R. R., Angew. Chem. Int. Chem., 2006, 45(16), 2546
Lai Y. L., Lii K. H., Wang S. L., J. Am. Chem. Soc., 2007, 129(17), 5350
Gordon L. E., Harrison W. T. A., Inorg. Chem., 2004, 43(6), 1808
Liu L., Zhang L. R., Wang X. F., Li G. H., Liu Y. L., Pang W. Q., Dalton Trans., 2008, 2009
Sheldrick G. M., SAINT, Bruker AXS Inc., Madison, WI, 2000
Sheldrick G. M., SHELXTL-97, Bruker AXS Inc., Madison, WI, 2000
Pan J. X., Zheng S. T., Yang G. Y., Crystal Growth & Design, 2005, 5(1), 237
Author information
Authors and Affiliations
Corresponding authors
Additional information
Supported by the National Natural Science Foundation of China (No.21271081).
Electronic supplementary material
Rights and permissions
About this article
Cite this article
Dong, Z., Yan, Y., Zhang, W. et al. Hydrothermal synthesis of a new zinc phosphite (C5H7N2)2·[Zn3(HPO3)4] with intersecting 8- and 12-ring channels. Chem. Res. Chin. Univ. 31, 498–502 (2015). https://doi.org/10.1007/s40242-015-5021-6
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s40242-015-5021-6