Abstract
Waterborne fluorinated polyurethane acrylate (WFPUA) with the different content of HEA were successfully obtained by introducing the fluorinated monomers both in polyurethane and polyacrylate. In our study, the particles size (d), viscosity (η) and the core-shell structure of WFPUA hybrid emulsion were characterized, the films were analyzed by Fourier transform infrared spectroscopy (FT-IR), and the surface energy, thermal stability and mechanical properties of the WFPUA films was characterized. The obtained results indicated that the increase of the HEA was benefit to the thermal stability, mechanical properties and antifouling ability of the WFPUA films. When the content of HEA were increased from the 0 % to 3.28 %, the water and methylene iodide contact angles increased from 101.8° to 121.1° and from 63.1° to 81.4°, respectively. And the tensile strength of the film samples were enhanced from 20.5 MPa to 30.32 MPa. At the same time, from the analysis of the DSC curves, the Tg has been improved. However, the increasing content of HEA has some negative effect on the migration of the fluorine element to the film surface from the analysis of XPS.
Similar content being viewed by others
References
Zhao XE, Ding JJ, Ye L (2014) Structure and solvent-resistant property of fluorinated polyurethane elastomer. J Fluor Chem 159:38–47
Wu GM, Kong ZW, Chen J, Huo SP, Liu GF (2014) Preparation and properties of waterborne polyurethane/epoxy resin composite coating from anionic terpene-based polyol dispersion. Progress in Organic Coatings 77:315–321
Deng JN, Gao J, Li H, Tan H, Zhang Q, Fu Q (2008) Mechanical and surface properties of polyurethane/fluorinated multi-walled carbon nanotubes composites. J Appl Polym Sci 108:2023–2028
Ge Z, Zhang XY, Dai JB, Li WH, Luo YJ (2009) Synthesis, characterization and properties of a novel fluorinated polyurethane. Eur Polym J 45:530–536
Zhou JH, Zhang L, Ma JZ (2013) Fluorinated polyacrylate emulsifier-free emulsion mediated by poly (acrylic acid)-b-poly (hexafluorobuthyl acrylate) trithiocarbonate via ab initio RAFT emulsion polymerization. Chem Eng J 223:8–17
Gao QZ, Li HQ, Zeng XR (2012) UV-curing of hyperbranched polyurethane acrylate-polyurethane diacrylate/SiO2 dispersion and TGA/FTIR study of cured films. J Polym Res 19:63–70
Ha H, Kin SC, Ha K (2010) UV curing kinetics and properties of polyurethane acrylate/muti-walled carbon nanotube coatings. J Polym Res 18:674–679
Jiang M, Zheng ZH, Ding XB, Cheng X, Peng YX (2007) Convenient synthesis of novel fluorinated polyurethane hybrid latex and core-shell structures via emulsion polymerization process with self-emulsification of polyurethane. Colloid Polym and Scie 285:1049–1054
Jiang M, Zhao XL, Ding XB, Zheng ZH, Peng YX (2005) A novel approach to fluorinated polyurethane by macromonomer copolymerization. Eur Polym J 41:1798–1803
Yang X, Zhu LQ, Yang Z, Chen YC, Bao BQ (2014) Surface properties and self-cleaning ability of the fluorinated acrylate coatings modified with dodecafluoroheptyl methacrylate though two adding ways. Appl Surf Sci 295:44–49
Liu S, Zhu G (2007) Effects of altered reaction conditions on the synthesis of polyurethane-poly (2,2,2-trifluoroethyl methacrylate) triblock copolymer aqueous dispersion. Eur Polym J 43:3904–3911
Shi R, Zhang XY, Dai JB (2010) Synthesis of fluorinated polyurethane/polyacrylate hybrid emulsion initiated by co-60 gamma-ray and properties of the latex film. Journal of Macromolecular Science Part a-Pure and Applied Chem 47:1104–1110
Canak TC (2013) Synthesis of fluorinated urethane acrylate based UV-curable coatings. Progress in Organic Coatings 76:388–399
Su T, Wang GY, Wang SL, Hu CP (2010) Fluorinated siloxane-containing waterborne polyurethaneureas with excellent hemocompatility, waterproof and mechanical properties. Eur Polym J 46:472–483
Xin H, Shen YD, Li XR (2011) Novel cationic polyurethane-fluorinated acrylic hybrid latexes:Synthesis, characterization and properties. Colloids and Surface A: Physicochemical and Engineering Aspects 384 (205–211)
Wang C, Li XR, Du B, Li PZ, Mi XH (2013) Effect of cationic monomer on properties of cationic fluorocarbon emulsifier-free emulsion. J Polym Res 20:1–9
Xu SP, Liu WQ (2008) Synthesis and surface characterization of an amphiphilic fluorinated copolymer via emulsifier-free emulsion polymerization of RAFT. J Fluor Chem 2:125–130
Shin MS, Lee YH, Rahman MM, Kim HD (2013) Synthesis and properties of water fluorinated polyurethane-acrylate using a solvent-/emulsifier- free method. Polymer 54:4873–4882
Zhang SF, Wang RM, He YF, Song PF, Wu ZM (2013) Waterborne polyurethane-acrylate copolymers crosslinked core-shell nanoparticles for jumidity-sensitive coatings. Progress in Organic Coatings 76:729–735
Jiang M, Zhao XL, Ding XB, Zheng ZH, Peng YX (2005) A novel approach to fluorinated polyurethane by macromonomer copolymerization. European Polymer Journal.41:1798–1803.
Wang YY, Qiu FX, Xu BB, Xu JC, Jiang Y, Yang DY, Li PL (2013) Preparation, mechanical properties and surface morphologies of waterborne fluorinated polyurethane-acrylate. Progress in Organic Coatings 76:876–883
Acknowledgements
We would like to express our great thanks to the National Natural Science Foundation of China (51373091), the National Natural Science Foundation of Shaanxi Province (2012JQ2004 and 2012JQ2005) and the academic backbone cultivation program of Shaanxi university of Science & technology (XSGP201212) for financial support.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Zhao, Z., Li, X., Li, P. et al. Study on properties of waterborne fluorinated polyurethane/acrylate hybrid emulsion and films. J Polym Res 21, 460 (2014). https://doi.org/10.1007/s10965-014-0460-1
Received:
Accepted:
Published:
DOI: https://doi.org/10.1007/s10965-014-0460-1