Abstract.
Nanocrystalline Ni 8 wt% doped TiO2 powder was synthesized by mechanical alloying. Microstructural and photo-spectrometiric analysis showed that the Ni added up to 8 wt% was dissolved into the rutile TiO2 matrix. The absorption threshold of the Ni doped powder shifted from 380 to 500 into the visible light region. (480–500 nm)
Similar content being viewed by others
References
S.J. Kim S.D. Park Y.H. Jeong S. Park (1999) J. Am. Ceram. Soc. 82 927 Occurrence Handle10.1111/j.1151-2916.1999.tb02014.x Occurrence Handle1:CAS:528:DyaK1MXisleisrs%3D
H. Gleiter (1992) Nanostruct. Mater. 1 1 Occurrence Handle1:CAS:528:DyaK38XktFahsLw%3D
D.W. Bahneman (1994) J. Phys. Chem. 98 1025
R. Wemberger P.B. Garber (1995) Appl. Phys. Lett. 66 2409
D. Madare M. Tasca M. Delibas G.I. Rusu (2000) Appl. Surf. Sci. 156 200
M.M. Rahman K.M. Krishna T. Soga T. Jimbo M. Umeno (1999) J. Phys. Chem. Solids 60 201 Occurrence Handle1:CAS:528:DyaK1MXhtVKnsr4%3D
K.M. Krishna M. Mosaddeq-ur-Rahman T. Miki K.M. Krishna T. Soga K. Igarashi S. Tanemura M. Umeno (1997) Appl. Surf. Sci. 113/114 149 Occurrence Handle1:CAS:528:DyaK2sXitVSqu78%3D
D.H. Kim, H.S. Hong, S.J. Kim, J.S. Song and K.S. Lee, J. Alloys Comp., in press (2004).
S.D. Park Y.H. Cho W.W. Kim S.J. Kim (1999) J. Solid State Chem. 146 230 Occurrence Handle1:CAS:528:DyaK1MXkvVOrtbk%3D
H.S. Kim S.I. Hong S.J. Kim (2001) J. Mater. Process. Technol. 112 109
Zhigang Zou Jinhua Ye H. Arakawa (2001) Solid State Commun. 119 471–475 Occurrence Handle1:CAS:528:DC%2BD3MXltFynurc%3D
K. Murali Krishna Md. Mosaddeq-ur-Rahman Takeshi Miki Tetsuo Soga Kazuo Igarashi Sakae Tanemura Masayoshi Umeno (1997) Appl. Surface Sci. 113/114 149–154
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Kim, D., Park, H.S., Kim, SJ. et al. Characteristics of Ni 8 wt%-doped titanium dioxide photocatalyst synthesized by mechanical alloying. Catal Lett 100, 49–52 (2005). https://doi.org/10.1007/s10562-004-3084-y
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/s10562-004-3084-y